喷射沉积6066Al/SiCp复合材料

来源期刊:中南大学学报(自然科学版)1997年第5期

论文作者:张豪 陈振华

文章页码:61 - 65

关键词:喷射沉积; 复合材料; 铝合金

Key words:spray deposition; composites; aluminum alloy

摘    要:采用多层喷射沉积技术制备了6066Al/SiCp板材和锭材,研究了轧制、挤压工艺和热处理制度对该材料组织和力学性能的影响。研究结果表明,SiC颗粒在基体中分布均匀,结合良好,界面无明显反应区;轧制和挤压是对喷射沉积材料有效的致密化工艺并能改善SiC颗粒在基体中的存在状态;材料在T6态获得拉伸强度为640MPa,屈服强度为580MPa,弹性模量为133GPs,延伸率为9.4%的优良力学性能。

Abstract: 6066Al/SiCp composites plates and billets are prepared by multi-layer spray deposition technology. The composites are then rolled or extruded and their mechanical properites in T6 condition are measured. The results show that the composites with uniform distribution of SiC particles and good interface bonding can be obtained. No apparent chemical reaction of interface is found. Rolling and extrusion are effective processes to improve material's density. SiC particles with sharp angle are possible to be broken into several small particles which may be the reason for the obvious decreasing of SiC particles' mean diameter after hot extrusion. The SiC particles become spherical and are more uniformly distributed. After extrusion of 14: 1 at 680K, the properties of the 6066Al/10%SiCp in T6 condition are: σb=640MPa, σ0.2=580MPa, E=133GPa, δ=9.4%. After rolling with reduction of 85% at 750K, the properties in T6 condition are: σb =414MPa, σ0.2=360MPa, δ=4.0% E=100GPa. The reseach shows that spray deposition is a good process to produce particle reinforced composites.



详情信息展示

 

<上一页 1 下一页 >

有色金属在线官网  |   会议  |   在线投稿  |   购买纸书  |   科技图书馆

中南大学出版社 主办 版权声明   电话:0731-88830515 88830516   传真:0731-88710482   Email:administrator@cnnmol.com

互联网出版许可证:新出网证(湘)字005号   湘ICP备09001153号