Adsorption of Re(Ⅶ) by coated solvent-impregnated resins containing Alamine 304-1 from sulfuric acid solutions
来源期刊:Rare Metals2020年第8期
论文作者:Xue-Yi Guo Zhong-Chen Ma Gao-Wei Liu Dong Li Qing-Hua Tian
文章页码:942 - 950
摘 要:The recovery of rhenium from waste acid is an urgent issue due to low rhenium concentration and high sulfuric acidity.To solve the problem,novel coated solvent-impregnated resins consisting of inert resins LS-300,Alamine 304-1 and the PVA film(304-CSIRs) were prepared for the separation of Re(Ⅶ) from high sulfuric acid solutions.It was shown that the PVA film coated completely on the surfaces of LS-300 resins with a thickness of 5 μm,and Alamine 304-1 distributed completely inside the porous of LS-300 resins.The adsorption fitted well with Langmuir model and pseudo-second-order model with the saturation adsorption capacity of139.40 mg·g-1.The maximum separation factor of Re(Ⅶ) versus Cu(Ⅱ) was up to 483,and 304-CSIRs had no adsorptions for As(V).The adsorption capacity of Re(Ⅶ) onto 304-CSIRs maintained in 97.79% at the fifth adsorption-desorption cycle.99.87% of rhenium was recovered by 304-CSIRs from waste acid generated from a copper smelter.
Xue-Yi Guo1,2,Zhong-Chen Ma1,2,Gao-Wei Liu1,2,Dong Li1,2,Qing-Hua Tian1,2
1. School of Metallurgy and Environment,Central South University2. National and Regional Joint Engineering Research Center of Nonferrous Metal Resource Recycling
摘 要:The recovery of rhenium from waste acid is an urgent issue due to low rhenium concentration and high sulfuric acidity.To solve the problem,novel coated solvent-impregnated resins consisting of inert resins LS-300,Alamine 304-1 and the PVA film(304-CSIRs) were prepared for the separation of Re(Ⅶ) from high sulfuric acid solutions.It was shown that the PVA film coated completely on the surfaces of LS-300 resins with a thickness of 5 μm,and Alamine 304-1 distributed completely inside the porous of LS-300 resins.The adsorption fitted well with Langmuir model and pseudo-second-order model with the saturation adsorption capacity of139.40 mg·g-1.The maximum separation factor of Re(Ⅶ) versus Cu(Ⅱ) was up to 483,and 304-CSIRs had no adsorptions for As(V).The adsorption capacity of Re(Ⅶ) onto 304-CSIRs maintained in 97.79% at the fifth adsorption-desorption cycle.99.87% of rhenium was recovered by 304-CSIRs from waste acid generated from a copper smelter.
关键词: