Effect of Nb on the corrosion behavior of continuous bulk metallic glass-coated steel wire composites
来源期刊:International Journal of Minerals Metallurgy and Materials2013年第6期
论文作者:Xiao-hua Chen Bao-yu Zhang Xi-dong Hui
文章页码:589 - 592
摘 要:(Zr41.2Ti13.8Cu12.5Ni10Be22.5 )100xNbx(at%, x=0 and 8) bulk metallic glasses (BMGs) were coated on the surface of Q195 steel wires by a continuous coating process. The potentiodynamic polarization tests of these BMGs were conducted in 3.5wt% NaCl aqueous solution. It is found that the addition of 8at% Nb into Zr 41.2Ti13.8Cu12.5Ni10Be22.5 alloy results in the improvement of corrosion resistance with the pitting potential of -52mV, the open circuit potential of -446mV, and the corrosion current density of 9.86×10 6 mA/cm2 . This may be attributed to that Nb is beneficial to passivate and stabilize Zr and Ti.
Xiao-hua Chen,Bao-yu Zhang,Xi-dong Hui
State Key Laboratory for Advanced Metals and Materials, University of Science and Technology Beijing
摘 要:(Zr41.2Ti13.8Cu12.5Ni10Be22.5 )100xNbx(at%, x=0 and 8) bulk metallic glasses (BMGs) were coated on the surface of Q195 steel wires by a continuous coating process. The potentiodynamic polarization tests of these BMGs were conducted in 3.5wt% NaCl aqueous solution. It is found that the addition of 8at% Nb into Zr 41.2Ti13.8Cu12.5Ni10Be22.5 alloy results in the improvement of corrosion resistance with the pitting potential of -52mV, the open circuit potential of -446mV, and the corrosion current density of 9.86×10 6 mA/cm2 . This may be attributed to that Nb is beneficial to passivate and stabilize Zr and Ti.
关键词: