BOF-LF-RH-CC流程生产38CrMoAl钢关键技术研究
来源期刊：钢铁2009年第12期
论文作者：赵克文 何生平 曾建华 王谦 王新华
文章页码：38 - 41
关键词：38CrMoAl钢； 精炼渣； 连铸保护渣； 洁净度
Key words：38CrMoAl steel； cleanliness； mold flux； refining slag
摘 要：38CrMoAl钢由于钢中[Al]含量极高(w([Al])为0.7%~1.1%),在连铸过程中容易导致水口的堵塞,同时在传统的高SiO2熔渣条件下,钢渣反应将导致钢水成分和熔渣性能发生较大的变化,恶化钢的洁净度。从热力学方面分析了高铝钢钢渣反应特性,得到了适合高铝钢的精炼渣和中间包保护渣成分控制目标,使钢中[Si]得到准确控制,钢的洁净度达到较高水平;同时采用高碱性高玻璃化连铸保护渣理论保证了熔渣吸收Al2O3夹杂后性能的稳定性。工业性试验结果表明:高铝钢铸坯平均w(T[O])<0.0012%,w([S])<0.003%,铸坯表面和皮下质量良好,完全满足用户要求。
Abstract: High in 38CrMoAl(w) of 0.7%-1.1%) is liable to cause the nozzle blockage in continuous casting process.The composition of molten steel as well as the properties of molten slag changed obviously because of the slag-steel reaction,which will worsen cleanliness of steel.Based on the analysis of slag-steel reaction characteristics by thermodynamics calculation,reasonable component and control range were analyzed for the component optimization of LF refining slag and tundish powder.In order to maintain stability of mold fluxes after absorbing Al2O3,high basic and high glass phase mold fluxes were used.The industrial experiment shows that the goal of w(T[O])<0.0012%,w([S])<0.003%,good surface and subsurface quality of blooms can be achieved.
赵克文1,2，何生平3，曾建华2，王谦2，王新华-1
(1.北京市北京科技大学 冶金与生态工程学院
2.四川省攀枝花市攀枝花钢铁集团公司
3.重庆大学 材料科学与工程学院，重庆 400044)
摘 要：38CrMoAl钢由于钢中[Al]含量极高(w([Al])为0.7%~1.1%),在连铸过程中容易导致水口的堵塞,同时在传统的高SiO2熔渣条件下,钢渣反应将导致钢水成分和熔渣性能发生较大的变化,恶化钢的洁净度。从热力学方面分析了高铝钢钢渣反应特性,得到了适合高铝钢的精炼渣和中间包保护渣成分控制目标,使钢中[Si]得到准确控制,钢的洁净度达到较高水平;同时采用高碱性高玻璃化连铸保护渣理论保证了熔渣吸收Al2O3夹杂后性能的稳定性。工业性试验结果表明:高铝钢铸坯平均w(T[O])<0.0012%,w([S])<0.003%,铸坯表面和皮下质量良好,完全满足用户要求。
关键词：38CrMoAl钢； 精炼渣； 连铸保护渣； 洁净度