Preparation of CePO4-coated zirconia ceramics and their mechanical behavior

来源期刊:Rare Metals2011年第3期

论文作者:ZI Weia, b, SU Cunpingc, LIN Yuanhuab, WANG Yonga, and DENG Xulianga a Department of VIP Dental Service, Peking University School and Hospital of Stomatology, Beijing , China b Department of Materials Science and Engineering, Tsinghua University, Beijing , China c Jiamusi University School and Hospital of Stomatology, Heilongjiang, Jiamusi , China

文章页码:282 - 286

摘    要:Tetragonal ZrO2-3 mol% Y2O3 (3Y-TZP) coated with CePO4 was synthesized by a co-precipitation method and the effects of CePO4 content and sintering temperature on its mechanical properties were investigated. The microstructure and phase composition of the products were characterized using scanning and transmission electron microscopy as well as X-ray diffraction, respectively. The machinability index of CePO4-coated zirconia was calculated to be 1.05 when the CePO4 content is 25 wt.%. The sample hardness, bending strength and fracture toughness are 7.08 GPa, 457.85 MPa and 9.75 MPa m1/2, respectively, when the sintering temperature is 1400°C. The results show that as-prepared CePO4-coated 3Y-TZP ceramics are highly suitable biomaterials for dental applications and are expected to be used in a com-puter-aided design and computer-aided manufacturing (CAD/CAM) system to make dental crowns or bridge prostheses in a one-step sinter-ing process.

详情信息展示

Preparation of CePO4-coated zirconia ceramics and their mechanical behavior

ZI Weia, b, SU Cunpingc, LIN Yuanhuab, WANG Yonga, and DENG Xulianga a Department of VIP Dental Service, Peking University School and Hospital of Stomatology, Beijing 100081, China b Department of Materials Science and Engineering, Tsinghua University, Beijing 100084, China c Jiamusi University School and Hospital of Stomatology, Heilongjiang, Jiamusi 154002, China

摘 要:Tetragonal ZrO2-3 mol% Y2O3 (3Y-TZP) coated with CePO4 was synthesized by a co-precipitation method and the effects of CePO4 content and sintering temperature on its mechanical properties were investigated. The microstructure and phase composition of the products were characterized using scanning and transmission electron microscopy as well as X-ray diffraction, respectively. The machinability index of CePO4-coated zirconia was calculated to be 1.05 when the CePO4 content is 25 wt.%. The sample hardness, bending strength and fracture toughness are 7.08 GPa, 457.85 MPa and 9.75 MPa m1/2, respectively, when the sintering temperature is 1400°C. The results show that as-prepared CePO4-coated 3Y-TZP ceramics are highly suitable biomaterials for dental applications and are expected to be used in a com-puter-aided design and computer-aided manufacturing (CAD/CAM) system to make dental crowns or bridge prostheses in a one-step sinter-ing process.

关键词:

<上一页 1 下一页 >

有色金属在线官网  |   会议  |   在线投稿  |   购买纸书  |   科技图书馆

中南大学出版社 技术支持 版权声明   电话:0731-88830515 88830516   传真:0731-88710482   Email:administrator@cnnmol.com

互联网出版许可证:(署)网出证(京)字第342号   京ICP备17050991号-6      京公网安备11010802042557号