Characteristic evaluation on spray-deposited WFTO thin films as a function of W doping ratio

来源期刊:Rare Metals2014年第4期

论文作者:G.Turgut E.F.Keskenler S.Aydin D.Tatar E.Sonmez S.Dogan B.Duzgun

文章页码:433 - 441

摘    要:In this work, F and F+W simultaneously doped SnO2 highly transparent conducting thin films were deposited on glass substrates at(500 ± 5) °C temperature by the spray pyrolysis method. Microstructural, morphological,electrical and optical properties of FTO films were investigated as a function of tungsten(W) doping, in the range from0 to 5 at%. X-ray diffraction patterns show that the films exhibit a tetragonal cassiterite structure and(200) preferential orientation of FTO film, and the relative strength of these peaks changes with altering the W doping ratio. The preferred growth of(211) changed to(200) plane with 2 at% W doping level and 3 at% W-doped film had(200) orientation and with further doping, this changed to(110) orientation.The scanning electron microscopy and atomic force microscopy images of the films indicate that the films are made up of dense small particles of a pyramidal shape and have a smooth surface. It was observed that the surface morphology of the films did not change much when the W element was inserted to the FTO structure. It was found that the sheet resistance values of the films varied with W doping ratio, and 2 at% W-doped FTO thin film exhibited the lowest values of sheet resistance(1.12 X). Also, the highest figure of merit, infrared reflectivity and optical band gap values were calculated for 2 at% W-doped FTO film as 50.9 9 10-2X-1,98.82 % and 4.13 eV, respectively. These results make the films an effective candidate for usage in many optoelectronic applications and photo-thermal conversion of solar energy.

详情信息展示

Characteristic evaluation on spray-deposited WFTO thin films as a function of W doping ratio

G.Turgut1,E.F.Keskenler2,S.Aydin1,D.Tatar1,E.Sonmez1,S.Dogan3,B.Duzgun1

1. Department of Physics Education,Kazim Karabekir Education Faculty,Atatürk University2. Department of Nanotechnology,Faculty of Engineering,Recep Tayyip Erdogan University3. Department of Electrical and Electronics Engineering,Faculty of Engineering and Architecture,Balikesir University

摘 要:In this work, F and F+W simultaneously doped SnO2 highly transparent conducting thin films were deposited on glass substrates at(500 ± 5) °C temperature by the spray pyrolysis method. Microstructural, morphological,electrical and optical properties of FTO films were investigated as a function of tungsten(W) doping, in the range from0 to 5 at%. X-ray diffraction patterns show that the films exhibit a tetragonal cassiterite structure and(200) preferential orientation of FTO film, and the relative strength of these peaks changes with altering the W doping ratio. The preferred growth of(211) changed to(200) plane with 2 at% W doping level and 3 at% W-doped film had(200) orientation and with further doping, this changed to(110) orientation.The scanning electron microscopy and atomic force microscopy images of the films indicate that the films are made up of dense small particles of a pyramidal shape and have a smooth surface. It was observed that the surface morphology of the films did not change much when the W element was inserted to the FTO structure. It was found that the sheet resistance values of the films varied with W doping ratio, and 2 at% W-doped FTO thin film exhibited the lowest values of sheet resistance(1.12 X). Also, the highest figure of merit, infrared reflectivity and optical band gap values were calculated for 2 at% W-doped FTO film as 50.9 9 10-2X-1,98.82 % and 4.13 eV, respectively. These results make the films an effective candidate for usage in many optoelectronic applications and photo-thermal conversion of solar energy.

关键词:

<上一页 1 下一页 >

相关论文

  • 暂无!

相关知识点

  • 暂无!

有色金属在线官网  |   会议  |   在线投稿  |   购买纸书  |   科技图书馆

中南大学出版社 技术支持 版权声明   电话:0731-88830515 88830516   传真:0731-88710482   Email:administrator@cnnmol.com

互联网出版许可证:(署)网出证(京)字第342号   京ICP备17050991号-6      京公网安备11010802042557号