An Oxygen-Permeation Treatment for Hardening Titanium Alloys

来源期刊:材料保护2004年增刊第2期

论文作者:WANG Mao-cai WEI Zheng MA Hong-yan XIN Gong-chun

关键词:oxygen permeation; titanium alloys; solution; hardening; performance;

摘    要:In this paper, the characterization of oxygen permeation (OP) in titanium alloy TC11 at high temperature and the influence of oxygen solution layer on performances of substrate were characterized with the help of apparatus, such as TGA,SEM/EDAX, XRD, EPMA, Micro-hardness Tester, Two-body Abrasion Tester, Amsler Wear Test Machine, Potentiostat/Galvanostat Model 273 system. The results showed that there was a little shift in X-ray diffraction peaks of α and β phase during the OPT process as a result of oxygen solution. The OP treatment can significantly increase the surface hardness of titanium alloys and, accordingly, the abrasive wear resistance was improved. Titanium alloys with oxygen solution layer exhibited improved corrosion resistance both in 3.5 % NaCl and in 5 % HCl solution. Oxidation resistance of TC11 with oxygen solution layer at high temperature was also enhanced. The solution and hardening mechanisms were discussed based on the experimental results.

详情信息展示

An Oxygen-Permeation Treatment for Hardening Titanium Alloys

WANG Mao-cai1,WEI Zheng2,MA Hong-yan1,XIN Gong-chun2

(1.State Key Laboratory for Corrosion and Protection, Institute of Metal Research, Chinese Academy of Sciences, Shenyang 110016;
2.Shenyang Liming Aero-engine Group Corporation, Shenyang 110043, P. R. China)

摘要:In this paper, the characterization of oxygen permeation (OP) in titanium alloy TC11 at high temperature and the influence of oxygen solution layer on performances of substrate were characterized with the help of apparatus, such as TGA,SEM/EDAX, XRD, EPMA, Micro-hardness Tester, Two-body Abrasion Tester, Amsler Wear Test Machine, Potentiostat/Galvanostat Model 273 system. The results showed that there was a little shift in X-ray diffraction peaks of α and β phase during the OPT process as a result of oxygen solution. The OP treatment can significantly increase the surface hardness of titanium alloys and, accordingly, the abrasive wear resistance was improved. Titanium alloys with oxygen solution layer exhibited improved corrosion resistance both in 3.5 % NaCl and in 5 % HCl solution. Oxidation resistance of TC11 with oxygen solution layer at high temperature was also enhanced. The solution and hardening mechanisms were discussed based on the experimental results.

关键词:oxygen permeation; titanium alloys; solution; hardening; performance;

【全文内容正在添加中】

<上一页 1 下一页 >

相关论文

  • 暂无!

相关知识点

  • 暂无!

有色金属在线官网  |   会议  |   在线投稿  |   购买纸书  |   科技图书馆

中南大学出版社 技术支持 版权声明   电话:0731-88830515 88830516   传真:0731-88710482   Email:administrator@cnnmol.com

互联网出版许可证:(署)网出证(京)字第342号   京ICP备17050991号-6      京公网安备11010802042557号