Preparation of New Cementitious System using Fly Ash and Dehydrated Autoclaved Aerated Concrete
来源期刊：Journal Of Wuhan University Of Technology Materials Science Edition2014年第4期
论文作者：水中和 LU Jianxin TIAN Sufang SHEN Peiliang DING Sha
文章页码：726 - 732
摘 要：We experimentally studied the interaction between pozzolanic material（fly ash） and dehydrated autoclaved aerated concrete（DAAC）. The DAAC powder was obtained by grinding aerated concrete waste to particles fi ner than 75μm and was then heated to temperatures up to 900 ℃. New cementitious material was prepared by proportioning fly ash and DAAC, named as AF. X-ray diffraction（XRD） was employed to identify the crystalline phases of DAAC before and after rehydration. The hydration process of AF was analyzed by the heat of hydration and non-evaporable water content（Wn）. The experimental results show that the highest reactivity of DAAC can be obtained by calcining the powder at 700 ℃ and the dehydrated products are mainly β-C2 S and CaO. The cumulative heat of hydration and Wn was found to be strongly dependent on the replacement level of fl y ash, increasing the replacement level of fl y ash lowered them in AF. The strength contribution rates on pozzolanic effect of fl y ash in AF are always negative, showing a contrary tendency of that of cement-fl y ash system.
水中和1，LU Jianxin2，TIAN Sufang2，SHEN Peiliang2，DING Sha2
1. State Key Laboratory of Silicate Materials for Architectures, Wuhan University of Technology2. School of Materials Science and Engineering, Wuhan University of Technology
摘 要：We experimentally studied the interaction between pozzolanic material（fly ash） and dehydrated autoclaved aerated concrete（DAAC）. The DAAC powder was obtained by grinding aerated concrete waste to particles fi ner than 75μm and was then heated to temperatures up to 900 ℃. New cementitious material was prepared by proportioning fly ash and DAAC, named as AF. X-ray diffraction（XRD） was employed to identify the crystalline phases of DAAC before and after rehydration. The hydration process of AF was analyzed by the heat of hydration and non-evaporable water content（Wn）. The experimental results show that the highest reactivity of DAAC can be obtained by calcining the powder at 700 ℃ and the dehydrated products are mainly β-C2 S and CaO. The cumulative heat of hydration and Wn was found to be strongly dependent on the replacement level of fl y ash, increasing the replacement level of fl y ash lowered them in AF. The strength contribution rates on pozzolanic effect of fl y ash in AF are always negative, showing a contrary tendency of that of cement-fl y ash system.