Oxide evolution in NdDy-Fe-B magnet during aging process
来源期刊:JOURNAL OF RARE EARTHS2012年第10期
论文作者:王景代 冯海波 李安华 李岩峰 朱明刚 李卫
文章页码:1020 - 1023
摘 要:Sintered NdDy-Fe-B magnets were made from strip cast flakes by powder metallurgy method. For the magnet with 6wt.% Dy substituted Nd, a remarkable coercivity increase of 70% was obtained after aging at 900°C for 2h and a high coercivity of 23.5 kOe was achieved after aging at 520°C for 2h. The average diameter of the oxide particles decreased during the following 900°C aging treatment. Dy and O diffusion from oxide particles to Nd-rich phase during the aging process was observed. The oxide evolution and Dy element diffusion were helpful to the coercivity enhancement.
王景代,冯海波,李安华,李岩峰,朱明刚,李卫
Division of Functional Materials, Central Iron and Steel Research Institute
摘 要:Sintered NdDy-Fe-B magnets were made from strip cast flakes by powder metallurgy method. For the magnet with 6wt.% Dy substituted Nd, a remarkable coercivity increase of 70% was obtained after aging at 900°C for 2h and a high coercivity of 23.5 kOe was achieved after aging at 520°C for 2h. The average diameter of the oxide particles decreased during the following 900°C aging treatment. Dy and O diffusion from oxide particles to Nd-rich phase during the aging process was observed. The oxide evolution and Dy element diffusion were helpful to the coercivity enhancement.
关键词: