Inhibition effects of benzalkonium chloride on Chlorella vulgaris induced corrosion of carbon steel
来源期刊:JOURNAL OF MATERIALS SCIENCE TECHNOLOG2020年第8期
论文作者:Junlei Wang Tiansui Zhang Xinxin Zhang Muhammed Asif Lipei Jiang Shuang Dong Tingyue Gu Hongfang Liu
文章页码:14 - 20
摘 要:In this work, a surfactant, benzalkonium chloride(BAC), was used to study its effects on both the growth of Chlorella vulgaris and the corrosion caused by its biofilm. Experimental results indicated that BAC at a low concentration of 3 mg/L suppressed C. vulgaris growth and achieved 81% corrosion inhibition based on weight loss reduction. The inhibition effects increased when the BAC dosage was increased.At 30 mg/L, the corrosion inhibition increased to 95%. Electrochemical results supported surface pitting analysis, weight loss results data and confirmed the corrosion inhibition.
Junlei Wang1,2,Tiansui Zhang1,Xinxin Zhang1,Muhammed Asif1,Lipei Jiang1,Shuang Dong3,Tingyue Gu2,Hongfang Liu1
1. School of Chemistry and Chemical Engineering, Huazhong University of Science and Technology2. Department of Chemical and Biomolecular Engineering, Institute for Corrosion and Multiphase Technology, Ohio University3. School of Chemical Engineering and Materials, Changzhou Institute of Technology
摘 要:In this work, a surfactant, benzalkonium chloride(BAC), was used to study its effects on both the growth of Chlorella vulgaris and the corrosion caused by its biofilm. Experimental results indicated that BAC at a low concentration of 3 mg/L suppressed C. vulgaris growth and achieved 81% corrosion inhibition based on weight loss reduction. The inhibition effects increased when the BAC dosage was increased.At 30 mg/L, the corrosion inhibition increased to 95%. Electrochemical results supported surface pitting analysis, weight loss results data and confirmed the corrosion inhibition.