Strength and Microstructure of Mortar Containing Glass Powder and/or Glass Aggregate
来源期刊:Journal Of Wuhan University Of Technology Materials Science Edition2016年第6期
论文作者:刘数华 WANG Shu ZHOU Wei LI Lihua XIAO Henglin WEI Jianpeng TANG Wan
文章页码:1302 - 1310
摘 要:The compressive strength of mortar containing glass powder(GP) and/or glass aggregate(GA) was tested, and its microstructure was also studied by thermogravimetric and differential thermal analysis(TG-DTA), scanning electron microscopy(SEM), energy dispersive spectroscopic analysis(EDX), and X-ray diffraction(XRD) techniques. The incorporation of GA would decrease the compressive strength of the mortar in the absence of GP. Incorporating both GA and GP could change the hydration environment, promote pozzolanic reaction of GP and improve the compressive strength. GP does not lead to but can effectively control ASR(Alkali Silica Reaction). GP and GA do not transform the type of hydrates, but have a great influence on the amounts of hydration products, and generate more calcium silicate hydrate(C-S-H gel) with lower Ca/Si ratio. GP and GA with good gradation will make the microstructure denser.
刘数华1,WANG Shu1,2,ZHOU Wei1,LI Lihua3,XIAO Henglin3,WEI Jianpeng1,TANG Wan1
1. State Key Laboratory of Water Resources and Hydropower Engineering Science,Wuhan University2. China Construction Ready Mixed Concrete Co.,Ltd.3. School of Civil Engineering and Architecture,Hubei University of Technology
摘 要:The compressive strength of mortar containing glass powder(GP) and/or glass aggregate(GA) was tested, and its microstructure was also studied by thermogravimetric and differential thermal analysis(TG-DTA), scanning electron microscopy(SEM), energy dispersive spectroscopic analysis(EDX), and X-ray diffraction(XRD) techniques. The incorporation of GA would decrease the compressive strength of the mortar in the absence of GP. Incorporating both GA and GP could change the hydration environment, promote pozzolanic reaction of GP and improve the compressive strength. GP does not lead to but can effectively control ASR(Alkali Silica Reaction). GP and GA do not transform the type of hydrates, but have a great influence on the amounts of hydration products, and generate more calcium silicate hydrate(C-S-H gel) with lower Ca/Si ratio. GP and GA with good gradation will make the microstructure denser.
关键词: