Mechanical properties and friction behaviors of CNT/AlSi10Mg composites produced by spark plasma sintering
来源期刊：International Journal of Minerals Metallurgy and Materials2017年第5期
论文作者：Lin-zhi Wang Ying Liu Jiao-jiao Wu Xi Zhang
文章页码：584 - 593
摘 要：The mechanical properties and friction behaviors of CNT/AlSi10Mg composites produced by spark plasma sintering（SPS） were investigated.The results showed that the densities of the sintered composites gradually increased with increasing sintering temperature and that the highest microhardness and compressive strength were achieved in the specimen sintered at 450°C.CNTs dispersed uniformly in the AlSi10Mg matrix when the addition of CNTs was less than 1.5wt%.However,when the addition of CNTs exceeded 1.5wt%,the aggregation of CNTs was clearly observed.Moreover,the mechanical properties（including the densities,compressive strength,and microhardness） of the composites changed with CNT content and reached a maximum value when the CNT content was 1.5wt%.Meanwhile,the minimum average friction coefficient and wear rate of the CNT/AlSi10Mg composites were obtained with 1.0wt% CNTs.
Lin-zhi Wang1,2，Ying Liu2，Jiao-jiao Wu1，Xi Zhang3
1. Chongqing Key Laboratory of Additive Manufacturing Technology and Systems,Chongqing Institute of Green and Intelligent Technology,Chinese Academy of Sciences2. College of Material Science and Engineering,Sichuan University3. College of Material Science and Engineering,Southwest Jiaotong university
摘 要：The mechanical properties and friction behaviors of CNT/AlSi10Mg composites produced by spark plasma sintering（SPS） were investigated.The results showed that the densities of the sintered composites gradually increased with increasing sintering temperature and that the highest microhardness and compressive strength were achieved in the specimen sintered at 450°C.CNTs dispersed uniformly in the AlSi10Mg matrix when the addition of CNTs was less than 1.5wt%.However,when the addition of CNTs exceeded 1.5wt%,the aggregation of CNTs was clearly observed.Moreover,the mechanical properties（including the densities,compressive strength,and microhardness） of the composites changed with CNT content and reached a maximum value when the CNT content was 1.5wt%.Meanwhile,the minimum average friction coefficient and wear rate of the CNT/AlSi10Mg composites were obtained with 1.0wt% CNTs.
关键词：