New ternary compound La8Al13Sn3
来源期刊:Rare Metals2009年第5期
论文作者:HE Weia, XIA Xiuwena, ZHANG Jilianga, HUANG Jinlia, b, and LIU Yixina a Key Laboratory of Nonferrous Metal Materials and New Processing Technology (Ministry of Education), College of Materials Science and Engineering, Guangxi Uni- versity, Nanning , China b Department of Physics and Electronic Information Science, Guangxi Teachers Education University, Nanning , China
文章页码:491 - 493
摘 要:A new ternary compound La8Al13Sn3 was synthesized and studied by means of X-ray powder diffraction technique. The compound La8Al13Sn3 crystallizes in a hexagonal AlB2-type structure with space group P6/mmm (No. 191) and the lattice parameters a = 0.44919(1) nm and c = 0.43835(1) nm. The Smith and Snyder figure of merit for index, FN, is F30 = 197.3(30). The Rietveld refinement for the crystal structure of the compound was carried out successfully. The liability R-factors of Rietveld refinement are Rp = 0.114 and Rwp = 0.148. The compound La8Al13Sn3 decomposes into LaAl2 with cubic structure and space group Fd 3m (227), LaAl3 with hexagonal structure and space group P63/mmc (194), and Sn at 720°C.
HE Weia, XIA Xiuwena, ZHANG Jilianga, HUANG Jinlia, b, and LIU Yixina a Key Laboratory of Nonferrous Metal Materials and New Processing Technology (Ministry of Education), College of Materials Science and Engineering, Guangxi Uni- versity, Nanning 530004, China b Department of Physics and Electronic Information Science, Guangxi Teachers Education University, Nanning 530023, China
摘 要:A new ternary compound La8Al13Sn3 was synthesized and studied by means of X-ray powder diffraction technique. The compound La8Al13Sn3 crystallizes in a hexagonal AlB2-type structure with space group P6/mmm (No. 191) and the lattice parameters a = 0.44919(1) nm and c = 0.43835(1) nm. The Smith and Snyder figure of merit for index, FN, is F30 = 197.3(30). The Rietveld refinement for the crystal structure of the compound was carried out successfully. The liability R-factors of Rietveld refinement are Rp = 0.114 and Rwp = 0.148. The compound La8Al13Sn3 decomposes into LaAl2 with cubic structure and space group Fd 3m (227), LaAl3 with hexagonal structure and space group P63/mmc (194), and Sn at 720°C.
关键词: