吉布森矿粉烧结试验研究
来源期刊：钢铁2010年第9期
论文作者：王颖生 吴胜利 赵志星 潘文
文章页码：14 - 17
关键词：吉布森矿粉； 同化性； 液相流动性； 烧结
Key words：MG fine； assimilation； liquid phase fluidity； sinter
摘 要：对一种低品质矿澳粉(吉布森矿粉,简称MGF)进行了研究。首先,通过微型烧结试验装置对该矿粉的高温特性进行了研究,在此基础上,对应用MGF的配矿方案进行了烧结杯试验。研究结果表明,MGF的同化性很高,液相流动性也较大,可以利用其特性与其他矿粉搭配烧结,弥补其SiO2和Al2O3含量较高、粒度组成较差的缺点。最后,通过工业生产实践,证明使用了6%MGF的烧结和高炉均运作良好。
Abstract: A low quality ore called MGF was researched for using in sinter process.Firstly,high temperature properties of ore were studied by micro sintering equipment,based on which,sinter pot test was carried out to verify the application of MGF.Results show that the assimilation and liquid phase fluidity of MGF both are high,which can be used as a measure to make up the disadvantage of that ore with high SiO2 and Al2O3 content and bad size composition.At last,through industrial practice,usage of MGF with ratio of 6% is feasible in sintering and blast furnace.
王颖生1,2，吴胜利1，赵志星1，潘文2
(1.北京市北京科技大学 冶金与生态工程学院
2.北京市首钢总公司)
摘 要：对一种低品质矿澳粉(吉布森矿粉,简称MGF)进行了研究。首先,通过微型烧结试验装置对该矿粉的高温特性进行了研究,在此基础上,对应用MGF的配矿方案进行了烧结杯试验。研究结果表明,MGF的同化性很高,液相流动性也较大,可以利用其特性与其他矿粉搭配烧结,弥补其SiO2和Al2O3含量较高、粒度组成较差的缺点。最后,通过工业生产实践,证明使用了6%MGF的烧结和高炉均运作良好。
关键词：吉布森矿粉； 同化性； 液相流动性； 烧结