摘    要:Scandia doped tungsten powders were prepared by spray drying combined with two-step hydrogen reduction.The particle size of doped tungsten powder,powder morphology and doped tungsten matrix were characterized by scanning electron microscope,X-ray diffrac-tion and laser diffraction particle size analyzer,respectively.The reduction behavior of Sc2O3 doped tungsten oxide and the effect of Sc2O3 on the property of tungsten powder were studied by the temperature programmed reduction.The experimental results showed that the pre-cursor powders prepared by spray drying had spherical shape.The addition of Sc2O3 could decrease the reduction temperature of tungsten oxide.The scandia doped tungsten powder had sub-micrometer size in the range of 0.1 to1 μm and scandium distributed evenly in the powder.By using this kind powder,sub-microstructure cathode matrices with semispherical grains and homogenous distribution of scan-dium were obtained.

详情信息展示

Effect of scandia on tungsten oxide powder reduction process

崔云涛,王金淑,刘伟,王茜

College of Materials Science and Engineering,Beijing University of Technology

摘 要:Scandia doped tungsten powders were prepared by spray drying combined with two-step hydrogen reduction.The particle size of doped tungsten powder,powder morphology and doped tungsten matrix were characterized by scanning electron microscope,X-ray diffrac-tion and laser diffraction particle size analyzer,respectively.The reduction behavior of Sc2O3 doped tungsten oxide and the effect of Sc2O3 on the property of tungsten powder were studied by the temperature programmed reduction.The experimental results showed that the pre-cursor powders prepared by spray drying had spherical shape.The addition of Sc2O3 could decrease the reduction temperature of tungsten oxide.The scandia doped tungsten powder had sub-micrometer size in the range of 0.1 to1 μm and scandium distributed evenly in the powder.By using this kind powder,sub-microstructure cathode matrices with semispherical grains and homogenous distribution of scan-dium were obtained.

关键词:

<上一页 1 下一页 >

相关论文

  • 暂无!

相关知识点

  • 暂无!

有色金属在线官网  |   会议  |   在线投稿  |   购买纸书  |   科技图书馆

中南大学出版社 技术支持 版权声明   电话:0731-88830515 88830516   传真:0731-88710482   Email:administrator@cnnmol.com

互联网出版许可证:(署)网出证(京)字第342号   京ICP备17050991号-6      京公网安备11010802042557号