Effects of N-alkylation on anticorrosion performance of doped polyaniline/epoxy coating
来源期刊：JOURNAL OF MATERIALS SCIENCE TECHNOLOG2020年第4期
论文作者：Suyun Liu Li Liu Ying Li Fuhui Wang
文章页码：48 - 55
摘 要：N-alkylation of sulfosalicylic acid-doped polyaniline（PANI-SSA） was used to promote the anticorrosion performance of PANI-SSA/epoxy coating for 5083 Al alloy. PANI-SSA was modified with C5H11Br and C12H25Br in polar solvents IPA（isopropanol） and DMF（dimethylformamide）, and then characterized by FTIR, XPS and sedimentation experiments. Results showed that alkanes were successfully linked onto the PANI-SSA chains. The compatibility between N-alkylated PANI-SSA and epoxy/xylene solution was improved. SEM results proved a better dispersion performance of N-alkylated PANI-SSA in epoxy coatings,with less holes and aggregations. Corrosion protection of the epoxy coatings incorporating PANI-SSA and N-alkylated PANI-SSA on 5083 Al alloy was studied by EIS and adhesion measurements in 3.5% NaCl solution. It turned out that the epoxy coating including C12H25Br-modified PANI-SSA in DMF has yielded the highest values of impedance modulus and best protective properties.
Suyun Liu1,2，Li Liu1,3，Ying Li1，Fuhui Wang1,3
1. Shenyang National Laboratory for Materials Science, Institute of Metal Research, Chinese Academy of Sciences2. School of Materials Science and Engineering, University of Science and Technology of China3. Key Laboratory for Anisotropy and Texture of Materials(Ministry of Education), School of Material Science and Engineering, Northeastern University
摘 要：N-alkylation of sulfosalicylic acid-doped polyaniline（PANI-SSA） was used to promote the anticorrosion performance of PANI-SSA/epoxy coating for 5083 Al alloy. PANI-SSA was modified with C5H11Br and C12H25Br in polar solvents IPA（isopropanol） and DMF（dimethylformamide）, and then characterized by FTIR, XPS and sedimentation experiments. Results showed that alkanes were successfully linked onto the PANI-SSA chains. The compatibility between N-alkylated PANI-SSA and epoxy/xylene solution was improved. SEM results proved a better dispersion performance of N-alkylated PANI-SSA in epoxy coatings,with less holes and aggregations. Corrosion protection of the epoxy coatings incorporating PANI-SSA and N-alkylated PANI-SSA on 5083 Al alloy was studied by EIS and adhesion measurements in 3.5% NaCl solution. It turned out that the epoxy coating including C12H25Br-modified PANI-SSA in DMF has yielded the highest values of impedance modulus and best protective properties.
关键词：