Structure and Electrical Conductivity of Compositely Doped Oxide Solid Electrolyte La0.8Sr0.2Ga0.8Mg0.12Co0.08O2.8
来源期刊:JOURNAL OF RARE EARTHS2007年增刊第1期
论文作者:Ma Xu Li Jianping Bao Juncheng Wang Zhiqi Zhao Jie Sun Jiashu
Key words:perovskite; ionic conductivity; solid state reaction; Lanthanum gallate; rare earths;
Abstract: (La, Sr) (Ga, Mg) O3-δ, (LSGM) perovskite compositions doped with transition metal Co on the B-site were prepared by solid state reaction. The effect of partial substitution of Ga for Co, La0.8Sr0.2Ga0.8Mg0.12Co0.08O2.8 (LSGMC2008) on the electrical conductivity was discussed. The results showed the compacted samples sintered at 1350℃ possesses increased electrical conductivity at low temperatures. The XRD patterns of the title materials indicated that LSGMC2008 possessed orthorhombic perovskite-type structure. The grains distributed relatively uniform from SEM photo. The Arrhenius plots of ionic conductivity in air of the LSGMC2008 exhibited differing slopes in the low-and high-temperature regions, and the corresponding Ea values were much lower than that of LSGM2020. All of these suggested that even at low sintering temperature, proper amount Co doped was beneficial to improve ionic conductivity of LSGM.
Ma Xu1,Li Jianping2,Bao Juncheng1,Wang Zhiqi1,Zhao Jie1,Sun Jiashu1
(1.School of Materials Science and Engineering, Tianjin University of Technology, Tianjin 300191, China;
2.Rolling Technique and Tandem Automation National Key Laboratory, Northeastern University, Shenyang 110004, China)
Abstract:(La, Sr) (Ga, Mg) O3-δ, (LSGM) perovskite compositions doped with transition metal Co on the B-site were prepared by solid state reaction. The effect of partial substitution of Ga for Co, La0.8Sr0.2Ga0.8Mg0.12Co0.08O2.8 (LSGMC2008) on the electrical conductivity was discussed. The results showed the compacted samples sintered at 1350℃ possesses increased electrical conductivity at low temperatures. The XRD patterns of the title materials indicated that LSGMC2008 possessed orthorhombic perovskite-type structure. The grains distributed relatively uniform from SEM photo. The Arrhenius plots of ionic conductivity in air of the LSGMC2008 exhibited differing slopes in the low-and high-temperature regions, and the corresponding Ea values were much lower than that of LSGM2020. All of these suggested that even at low sintering temperature, proper amount Co doped was beneficial to improve ionic conductivity of LSGM.
Key words:perovskite; ionic conductivity; solid state reaction; Lanthanum gallate; rare earths;
【全文内容正在添加中】