Orientation Dependence of the Micro-Pillar Compression Strength in an Electron Beam Melted Ti–6Al–4V Alloy
来源期刊：Acta Metallurgica Sinica2021年第4期
论文作者：Jinsen Tian Jiang Ma Ming Yan Zhuo Chen Jun Shen Jing Wu
文章页码：476 - 484
摘 要：An α/β two-phase Ti-6 Al-4 V alloy was fabricated by electron beam melting to obtain a basketweave structure.The orientation dependence of the mechanical properties of Ti-6 Al-4 V alloy was studied by micro-pillar compression and post-mortem transmission electron microscopy analysis.The results indicate that different grains have different mechanical responses,and the possible attributions were discussed.Besides the orientation effect,due to the limited volumes of micropillars,the size of the a phases,dispersion of the β phases,and the presence of the free dislocation path also affect the mechanical properties of the micropillars to a large extent.Although no direct link was discovered between the mechanical properties and the parent βorientations,this work provided a promising method to further study the anisotropic mechanical behavior in Ti-6 Al-4 V alloy.
Jinsen Tian1，Jiang Ma1，Ming Yan2，Zhuo Chen3，Jun Shen1，Jing Wu4
1. College of Mechatronics and Control Engineering,Shenzhen University2. Department of Materials Science and Engineering and Shenzhen Key Laboratory for Additive Manufacturing of High-Performance Materials,Southern University of Science and Technology3. Aerospace Hiwing (Harbin) Titanium Industrial Co.,Ltd.4. Cryo-EM Center,Southern University of Science and Technology
摘 要：An α/β two-phase Ti-6 Al-4 V alloy was fabricated by electron beam melting to obtain a basketweave structure.The orientation dependence of the mechanical properties of Ti-6 Al-4 V alloy was studied by micro-pillar compression and post-mortem transmission electron microscopy analysis.The results indicate that different grains have different mechanical responses,and the possible attributions were discussed.Besides the orientation effect,due to the limited volumes of micropillars,the size of the a phases,dispersion of the β phases,and the presence of the free dislocation path also affect the mechanical properties of the micropillars to a large extent.Although no direct link was discovered between the mechanical properties and the parent βorientations,this work provided a promising method to further study the anisotropic mechanical behavior in Ti-6 Al-4 V alloy.