Refill friction stir spot welding of 5083-O aluminum alloy
来源期刊：JOURNAL OF MATERIALS SCIENCE TECHNOLOG2018年第5期
论文作者：Zhiwu Xu Zhengwei Li Shude Ji Liguo Zhang
文章页码：878 - 885
摘 要：In this work,refill friction stir spot welding（RFSSW） was used to weld 2 mm-thick 5083-O alloy.The Box–Behnken experimental design was used to investigate the effect of welding parameters on the joint lap shear property.Results showed that a surface indentation of 0.3 mm effectively eliminated the welding defects.Microhardness of the stir zone（SZ） was higher than that of the base material（BM） and the hardness decreased with increasing the heat input during welding.The optimum failure load of 7.72 k N was obtained when using rotating speed of 2300 rpm,plunge depth of 2.4 mm and refilling time of 3.5 s.Three fracture modes were obtained during the lap shear test and all were affected by the hook defect.
Zhiwu Xu1，Zhengwei Li1，Shude Ji2，Liguo Zhang2
1. State Key Laboratory of Advanced Welding and Joining,Harbin Institute of Technology2. Faculty of Aerospace Engineering,Shenyang Aerospace University
摘 要：In this work,refill friction stir spot welding（RFSSW） was used to weld 2 mm-thick 5083-O alloy.The Box–Behnken experimental design was used to investigate the effect of welding parameters on the joint lap shear property.Results showed that a surface indentation of 0.3 mm effectively eliminated the welding defects.Microhardness of the stir zone（SZ） was higher than that of the base material（BM） and the hardness decreased with increasing the heat input during welding.The optimum failure load of 7.72 k N was obtained when using rotating speed of 2300 rpm,plunge depth of 2.4 mm and refilling time of 3.5 s.Three fracture modes were obtained during the lap shear test and all were affected by the hook defect.
关键词：