Ceramsite Containing Iron Oxide and its Use as Functional Aggregate in Microwave Absorbing Cement-based Materials
来源期刊:Journal Of Wuhan University Of Technology Materials Science Edition2018年第1期
论文作者:何永佳 LI Guangfeng Lü Linnü HE Liu
文章页码:133 - 138
摘 要:Electromagnetic(EM) wave absorbing cement-based composite has promising applications in protecting civil and military buildings from electromagnetic interferences. A new idea of preparing EM wave absorbing cement-based composite is proposed by using ceramsite containing iron oxide as EM wave absorbing functional aggregate. The ceramsite was synthesized by adding 10 wt% Fe3O4 into clay and sintering at 1 200 ℃, which shows obvious dielectric and magnetic loss properties for electromagnetic wave. The maximum reflection loss(RL) of the concrete specimens prepared with the ceramsite is between-10.2--10.7 dB(corresponding to absorption greater than 90% EM energy) in the bandwidth of 8-18 GHz. In addition, the compressive strength at 28 days age of the concrete is 46 MPa, showing the potentiality of being used as structural components in buildings.
何永佳1,2,LI Guangfeng2,Lü Linnü3,HE Liu4
1. State Key Laboratory of Silicate Materials for Architectures, Wuhan University of Technology2. School of Materials Science and Engineering, Wuhan University of Technology3. Hubei Key Laboratory of Theory and Application of Advanced Materials Mechanics, School of Science, Wuhan University of Technology4. China Railway Eleventh Bureau Group Fifth Engineering Co., Ltd.
摘 要:Electromagnetic(EM) wave absorbing cement-based composite has promising applications in protecting civil and military buildings from electromagnetic interferences. A new idea of preparing EM wave absorbing cement-based composite is proposed by using ceramsite containing iron oxide as EM wave absorbing functional aggregate. The ceramsite was synthesized by adding 10 wt% Fe3O4 into clay and sintering at 1 200 ℃, which shows obvious dielectric and magnetic loss properties for electromagnetic wave. The maximum reflection loss(RL) of the concrete specimens prepared with the ceramsite is between-10.2--10.7 dB(corresponding to absorption greater than 90% EM energy) in the bandwidth of 8-18 GHz. In addition, the compressive strength at 28 days age of the concrete is 46 MPa, showing the potentiality of being used as structural components in buildings.