Improvement of coercivity and corrosion resistance of Nd-Fe-B sintered magnets by doping aluminium nano-particles

来源期刊:Journal of Rare Earths2013年第1期

论文作者:刘卫强 孙超 岳明 孙浩 张东涛 张久兴

文章页码:65 - 68

摘    要:Nd-Fe-B permanent magnets with a small amount of Al nano-particles doping were prepared by conventional sintered method. Effect of Al content on magnetic property, corrosion resistance and oxidation properties of the magnets were studied. Investigation showed that the coercivity rose gradually, while the remanence decreased simultaneously with increase of Al doping amount. Further investigation revealed that most Al element diffused into the main phase and some Al element diffused into the Nd-rich phase. The autoclave test results showed that the corrosion rate of the magnets decreased with Al content increasing. After oxidation, the maximum energy product losses of the magnets with 0.0 wt.% and 0.2 wt.% Al nano-particles doping were 6.13% and 3.99%, respectively. Therefore, Al nano-particles doping was a promising way to enhance the coercivity and corrosion resistance of sintered Nd-Fe-B magnet.

详情信息展示

Improvement of coercivity and corrosion resistance of Nd-Fe-B sintered magnets by doping aluminium nano-particles

刘卫强1,孙超1,岳明1,孙浩1,张东涛1,张久兴1

1. College of Materials Science and Engineering,Beijing University of Technology

摘 要:Nd-Fe-B permanent magnets with a small amount of Al nano-particles doping were prepared by conventional sintered method. Effect of Al content on magnetic property, corrosion resistance and oxidation properties of the magnets were studied. Investigation showed that the coercivity rose gradually, while the remanence decreased simultaneously with increase of Al doping amount. Further investigation revealed that most Al element diffused into the main phase and some Al element diffused into the Nd-rich phase. The autoclave test results showed that the corrosion rate of the magnets decreased with Al content increasing. After oxidation, the maximum energy product losses of the magnets with 0.0 wt.% and 0.2 wt.% Al nano-particles doping were 6.13% and 3.99%, respectively. Therefore, Al nano-particles doping was a promising way to enhance the coercivity and corrosion resistance of sintered Nd-Fe-B magnet.

关键词:

<上一页 1 下一页 >

有色金属在线官网  |   会议  |   在线投稿  |   购买纸书  |   科技图书馆

中南大学出版社 技术支持 版权声明   电话:0731-88830515 88830516   传真:0731-88710482   Email:administrator@cnnmol.com

互联网出版许可证:(署)网出证(京)字第342号   京ICP备17050991号-6      京公网安备11010802042557号