薄板坯连铸连轧取向硅钢流程中Cu2S抑制剂的析出行为
来源期刊：钢铁2009年第11期
论文作者：项利 岳尔斌 仇圣桃 赵沛
文章页码：79 - 82
关键词：取向硅钢； 薄板坯连铸连轧； 抑制剂； Cu2S； 析出
Key words：grain oriented silicon steel； thin slab casting and rolling； inhibitor； Cu2S； precipitation
摘 要：研究了Cu2S抑制剂在薄板坯连铸连轧流程生产取向硅钢全流程中的析出特点。结果表明:典型成分取向硅钢主抑制剂Cu2S在全工序进程中析出粒子呈不断长大的趋势,粒子分布密度与体积分数在高温退火前也不断增加,高温退火净化后,剩余粒子变大,分布密度大大降低,对应体积分数也降低。
Abstract: The whole process’s precipitated characteristics of inhibitor(Cu2S) in the grain oriented silicon steel produced by the thin slab casting and rolling process were studied.The results indicate that the main inhibitor(Cu2S) of CGO steel with typical composition continuously grows in the whole process;The distribution density and volume fraction of Cu2S continuously increase before the high temperature annealing process;After the purification treatment in high temperature annealing process,residual Cu2S grows and the distribution density and volume fraction of Cu2S decreased greatly.
项利1，岳尔斌1，仇圣桃1，赵沛1
(1.北京市钢铁研究总院连铸技术国家工程研究中心)
摘 要：研究了Cu2S抑制剂在薄板坯连铸连轧流程生产取向硅钢全流程中的析出特点。结果表明:典型成分取向硅钢主抑制剂Cu2S在全工序进程中析出粒子呈不断长大的趋势,粒子分布密度与体积分数在高温退火前也不断增加,高温退火净化后,剩余粒子变大,分布密度大大降低,对应体积分数也降低。
关键词：取向硅钢； 薄板坯连铸连轧； 抑制剂； Cu2S； 析出