摘    要:The phase evolution and magnetic properties of Nd9?xYxFe72Ti2Zr2B15 (x = 0,0.5,1,and 2) melt-spun nanocomposite ribbons were studied.It is found that Y addition not only enhances the formability of amorphous phase in the alloy,but also stabilizes the amorphous phase during the annealing treatment.The appropriate content of Y addition effectively enhances the remanence (Jr) of the annealed sample.The residual amorphous intergranular phase in the annealed sample optimizes the squareness of the loop,resulting in an larger maximum energy product (BH)max.The best magnetic properties,Jr = 0.78 T,Hci (coercivity) = 923.4 kA/m,and (BH)max = 98.5 kJ/m3,were obtained from the Nd8YFe72Ti2Zr2B15 ribbon spun at Vs = 4 m/s and annealed at 700°C for 10 min,which is composed of Nd2Fe14B,α-Fe,and amorphous phase.

详情信息展示

Magnetic properties of Nd2Fe14B/α-Fe nanocomposite magnets with yttrium addition

CHEN Zhi’ana,SUI Yanlib,and GUO Zhimenga a Institute of Powder Metallurgy,University of Science and Technology Beijing,Beijing 100083,China b State Key Laboratory for Advanced Metals and Materials,University of Science and Technology Beijing,Beijing 100083,China

摘 要:The phase evolution and magnetic properties of Nd9?xYxFe72Ti2Zr2B15 (x = 0,0.5,1,and 2) melt-spun nanocomposite ribbons were studied.It is found that Y addition not only enhances the formability of amorphous phase in the alloy,but also stabilizes the amorphous phase during the annealing treatment.The appropriate content of Y addition effectively enhances the remanence (Jr) of the annealed sample.The residual amorphous intergranular phase in the annealed sample optimizes the squareness of the loop,resulting in an larger maximum energy product (BH)max.The best magnetic properties,Jr = 0.78 T,Hci (coercivity) = 923.4 kA/m,and (BH)max = 98.5 kJ/m3,were obtained from the Nd8YFe72Ti2Zr2B15 ribbon spun at Vs = 4 m/s and annealed at 700°C for 10 min,which is composed of Nd2Fe14B,α-Fe,and amorphous phase.

关键词:

<上一页 1 下一页 >

相关论文

  • 暂无!

相关知识点

  • 暂无!

有色金属在线官网  |   会议  |   在线投稿  |   购买纸书  |   科技图书馆

中南大学出版社 技术支持 版权声明   电话:0731-88830515 88830516   传真:0731-88710482   Email:administrator@cnnmol.com

互联网出版许可证:(署)网出证(京)字第342号   京ICP备17050991号-6      京公网安备11010802042557号