Investigation on Preparation and Fluorescence Properties of Oxy-Fluoride Glass Co-Doped with Er3+ and Yb3+
来源期刊:JOURNAL OF RARE EARTHS2004年第4期
论文作者:杨魁胜 程光 梁海莲 孟健
Key words:oxy-fluoride glass; Yb3+/Er3+; fusion method; spectrum; rare earths;
Abstract: The glass sample based on the composition of 45PbF2-45GeO2-10WO3 co-doped with Yb3+/Er3+ was prepared by the fusion method in two steps: melted at 950 ℃ for 20~25 min then annealed at 380 ℃ for 4 h. Through the V-prism it is found that the refractive index of host glass and the sample are 1.517 and 1.65 respectively. The transmittance was observed by using the ultraviolet-visible-infrared spectrometer in the wavelength range from 0.35 to 2.5μm. The transmittance of the host glass is beyond 73%. That of the sample is beyond 50% and there are characteristic absorption peaks of rare-earth ions. The emission spectrum was measured by using the Hitachi F-4500 fluorescent spectrometer pumped by 980 nm semiconductor laser. There are a strong emission peak at 530 nm and a weak peak at 650 nm.
杨魁胜1,程光1,梁海莲1,孟健2
(1.School of Material and Chemical Engineering,Changchun University of Science and Technology,Changchun 130022,China;
2.Key Laboratory of Rare Earth Chemistry and Physics,Changchun Institute of Applied Chemistry,Chinese Academy of Sciences,Changchun 130021,China)
Abstract:The glass sample based on the composition of 45PbF2-45GeO2-10WO3 co-doped with Yb3+/Er3+ was prepared by the fusion method in two steps: melted at 950 ℃ for 20~25 min then annealed at 380 ℃ for 4 h. Through the V-prism it is found that the refractive index of host glass and the sample are 1.517 and 1.65 respectively. The transmittance was observed by using the ultraviolet-visible-infrared spectrometer in the wavelength range from 0.35 to 2.5μm. The transmittance of the host glass is beyond 73%. That of the sample is beyond 50% and there are characteristic absorption peaks of rare-earth ions. The emission spectrum was measured by using the Hitachi F-4500 fluorescent spectrometer pumped by 980 nm semiconductor laser. There are a strong emission peak at 530 nm and a weak peak at 650 nm.
Key words:oxy-fluoride glass; Yb3+/Er3+; fusion method; spectrum; rare earths;