Fabrication and Mechanical Properties of Al2O3/TiAl Composites
来源期刊：Journal Of Wuhan University Of Technology Materials Science Edition2009年第5期
论文作者：艾桃桃
文章页码：732 - 735
摘 要：Al2O3/TiAl composites were successfully fabricated by hot-press-assisted exothermic dispersion method with elemental powder mixtures of Ti, Al TiO2 and Nb2O5, and the microstructure and mechanical properties were investigated. The results indicate the fine Al2O3 particles tend to disperse on the grain boundaries. The grain size of TiAl matrix decreases and the hardness increases with increasing Nb2O5 content. The bending strength and fracture toughness reach to a maximum when Nb2O5 content is 6 wt%, under 642 MPa and 6.69 MPa·m1/2, respectively. Based on the fractography and the observation of crack propagation path, it is concluded that the strengthening and toughening of such composites at room temperature can be attributed to the refinement of the TiAl matrix, the deflection behavior in the crack propagation and the dispersion of Al2O3 particles.
艾桃桃
Department of Materials Science and Engineering,Shaanxi University of Technology
摘 要：Al2O3/TiAl composites were successfully fabricated by hot-press-assisted exothermic dispersion method with elemental powder mixtures of Ti, Al TiO2 and Nb2O5, and the microstructure and mechanical properties were investigated. The results indicate the fine Al2O3 particles tend to disperse on the grain boundaries. The grain size of TiAl matrix decreases and the hardness increases with increasing Nb2O5 content. The bending strength and fracture toughness reach to a maximum when Nb2O5 content is 6 wt%, under 642 MPa and 6.69 MPa·m1/2, respectively. Based on the fractography and the observation of crack propagation path, it is concluded that the strengthening and toughening of such composites at room temperature can be attributed to the refinement of the TiAl matrix, the deflection behavior in the crack propagation and the dispersion of Al2O3 particles.
关键词：