Fluxing Agents on Ceramification of Composites of MgO-Al2O3-SiO2/Boron Phenolic Resin
来源期刊:Journal Of Wuhan University Of Technology Materials Science Edition2018年第2期
论文作者:石敏先 CHEN Xia FAN Shanshan SHEN Shirley LIU Tianxiang 黄志雄
文章页码:381 - 388
摘 要:Fluxing agents of zinc borate, antimony oxide, galss frit A and glass frit B, with different melting or softening point temperatures, were added into MgO-Al2O3-SiO2/boron phenol formaldehyde resin(MAS/BPF) composites to lower the formation temperature of eutectic liquid phase and promote the ceramification of ceramifiable composites. The effects of fluxing agents on the thermogravimetric properties, phase evolution, and microstructure evolution of MAS/BPF composites were characterized by TG-DSC, XRD and SEM analyses. The results reveal that the addition of a fluxing agent highly reduces the decomposition rate of MAS/BPF composites. Fluxing agents lower the formation temperatures of liquid phases of ceramifiable MAS/BPF composites obviously, and then promote the ceramification and densification process. The final residues of composites are ceramic surrounded by large amount of glass phases.
石敏先1,CHEN Xia1,FAN Shanshan1,SHEN Shirley2,LIU Tianxiang1,黄志雄1
1. School of Materials Science and Engineering,Wuhan University of Technology2. CSIRO Manufacturing
摘 要:Fluxing agents of zinc borate, antimony oxide, galss frit A and glass frit B, with different melting or softening point temperatures, were added into MgO-Al2O3-SiO2/boron phenol formaldehyde resin(MAS/BPF) composites to lower the formation temperature of eutectic liquid phase and promote the ceramification of ceramifiable composites. The effects of fluxing agents on the thermogravimetric properties, phase evolution, and microstructure evolution of MAS/BPF composites were characterized by TG-DSC, XRD and SEM analyses. The results reveal that the addition of a fluxing agent highly reduces the decomposition rate of MAS/BPF composites. Fluxing agents lower the formation temperatures of liquid phases of ceramifiable MAS/BPF composites obviously, and then promote the ceramification and densification process. The final residues of composites are ceramic surrounded by large amount of glass phases.