Preparation of Ultra-light Xonotlite Thermal Insulation Material Using Carbide Slag
来源期刊：Journal Of Wuhan University Of Technology Materials Science Edition2010年第2期
论文作者：刘飞 曹建新
文章页码：295 - 297
摘 要：Using carbide slag as the calcareous materials, xonotlite thermal insulation material was successfully prepared via dynamic hydrothermal synthesis. The experimental results show that the xonotlite thermal insulation material is made up of large numbers of "chestnut bur shape" particles. Optimum conditions of calcination temperature of carbide slag, synthesis reaction temperature and time, stirring rate, CaO/SiO2 mol ratio, water/solid weight ratio, amount of fiberglass, molding pressures, dryness temperatures and the presence of dispersant （glycol and polyvinyl alcohol） favor the preparation of xonotlite thermal insulation material. The evaluation of xonotlite thermal insulation material reveals that the product is ultra-light and excellent in physical performances. Such a little amount of impurities in carbide slag has no effect on the phase, morphology, stability at high temperature and physical performances of products.
刘飞1,2，曹建新2
1. ollege of Materials Science and Engineering, South China University of Technology2. School Chemistry and Chemical Engineering, Guizhou University
摘 要：Using carbide slag as the calcareous materials, xonotlite thermal insulation material was successfully prepared via dynamic hydrothermal synthesis. The experimental results show that the xonotlite thermal insulation material is made up of large numbers of "chestnut bur shape" particles. Optimum conditions of calcination temperature of carbide slag, synthesis reaction temperature and time, stirring rate, CaO/SiO2 mol ratio, water/solid weight ratio, amount of fiberglass, molding pressures, dryness temperatures and the presence of dispersant （glycol and polyvinyl alcohol） favor the preparation of xonotlite thermal insulation material. The evaluation of xonotlite thermal insulation material reveals that the product is ultra-light and excellent in physical performances. Such a little amount of impurities in carbide slag has no effect on the phase, morphology, stability at high temperature and physical performances of products.
关键词：