Preparation and Surface Properties of Silicon-Containing Waterborne Polyurethane Functionalized with Fluorine-Containing Acrylate and Micro-Nano Silica
来源期刊：Journal Of Wuhan University Of Technology Materials Science Edition2018年第1期
论文作者：蔡棋 HUANG Jiemin 翁睿 LIU Shichen
文章页码：233 - 241
摘 要：In order to prepare hydrophobic waterborne polyurethane coatings with better performances, the silicon-containing waterborne polyurethane（SiWPU） with functional chain extender hydroxyethyl acrylate（HEA） was prepared first, and then a series of silicon&fluorine-containing polyurethane/acrylate（FSiPUA） emulsions were obtained with flourine containing acrylic monomer by seed emulsion polymerization, introducing micro-nano SiO2 into FSiPUA emulsion to make the final hybrid emulsion. The properties of Si WPU, FSiPUA and SiO2/FSiPUA were investigated by fourier transform infrared spectra（FTIR）, transmission electron microscope（TEM）, Scanning Electron Microscope（SEM） and some other analytical methods. The results revealed that FSiPUA emulsion particles possessed composite core-shell structure and FSiPUA films with suitable ratio performed better than Si WPU films in hardness, water resistance and solvent resistance. The SiO2/FSiPUA films with micro-nano dual roughness structure showed a water contact angle of 136° with good resistance to acid and alkali.
蔡棋，HUANG Jiemin，翁睿，LIU Shichen
School of Materials Science and Engineering, Wuhan University of Technology
摘 要：In order to prepare hydrophobic waterborne polyurethane coatings with better performances, the silicon-containing waterborne polyurethane（SiWPU） with functional chain extender hydroxyethyl acrylate（HEA） was prepared first, and then a series of silicon&fluorine-containing polyurethane/acrylate（FSiPUA） emulsions were obtained with flourine containing acrylic monomer by seed emulsion polymerization, introducing micro-nano SiO2 into FSiPUA emulsion to make the final hybrid emulsion. The properties of Si WPU, FSiPUA and SiO2/FSiPUA were investigated by fourier transform infrared spectra（FTIR）, transmission electron microscope（TEM）, Scanning Electron Microscope（SEM） and some other analytical methods. The results revealed that FSiPUA emulsion particles possessed composite core-shell structure and FSiPUA films with suitable ratio performed better than Si WPU films in hardness, water resistance and solvent resistance. The SiO2/FSiPUA films with micro-nano dual roughness structure showed a water contact angle of 136° with good resistance to acid and alkali.
关键词：