High Temperature Stress Rupture Anisotropy of a Ni-Based Single Crystal Superalloy
来源期刊：JOURNAL OF MATERIALS SCIENCE TECHNOLOG2016年第10期
论文作者：Guanglei Wang Jinlai Liu Jide Liu Tao Jin Xiaofeng Sun Xudong Sun Zhuangqi Hu
文章页码：1003 - 1007
摘 要：High temperature stress rupture anisotropies of a second generation Ni-base single crystal（SC） superalloy specimens with [001], [011] and [111] orientations under 900 ℃/445 MPa and 1100 ℃/100 MPa have been investigated in the present study, with attentions to the evolution of γ/γ′ microstructure observed by scanning electron microscopy and the dislocation configuration characterized by transmission electron microscopy in each oriented specimen. At 1100 ℃/100 MPa as well as 900 ℃/445 MPa, the single crystal superalloy exhibits obvious stress rupture anisotropic behavior. The [001] oriented specimen has the longest rupture lifetime at 900 ℃/445 MPa, and the [111] oriented sample shows the best rupture strength at 1100 ℃/100 MPa. While the [011] oriented specimen presents the worst rupture lifetime at each testing condition, its stress rupture property at 1100 ℃/100 MPa is clearly improved, compared with900 ℃/445 MPa. The evident stress rupture anisotropy at 900 ℃/445 MPa is mainly attributed to the distinctive movement way of dislocations in each oriented sample. Whereas, at 1100 ℃/100 MPa, together with the individual dislocation configuration, the evolution of γ/γ′ microstructure in each orientation also plays a key role in the apparent stress rupture anisotropy.
Guanglei Wang1,2，Jinlai Liu1，Jide Liu1，Tao Jin1，Xiaofeng Sun1，Xudong Sun2，Zhuangqi Hu1,2
1. Superalloy Division, Institute of Metal Research, Chinese Academy of Sciences2. Key Laboratory of Anisotropy and Texture of Materials (Ministry of Education), Northeastern University
摘 要：High temperature stress rupture anisotropies of a second generation Ni-base single crystal（SC） superalloy specimens with [001], [011] and [111] orientations under 900 ℃/445 MPa and 1100 ℃/100 MPa have been investigated in the present study, with attentions to the evolution of γ/γ′ microstructure observed by scanning electron microscopy and the dislocation configuration characterized by transmission electron microscopy in each oriented specimen. At 1100 ℃/100 MPa as well as 900 ℃/445 MPa, the single crystal superalloy exhibits obvious stress rupture anisotropic behavior. The [001] oriented specimen has the longest rupture lifetime at 900 ℃/445 MPa, and the [111] oriented sample shows the best rupture strength at 1100 ℃/100 MPa. While the [011] oriented specimen presents the worst rupture lifetime at each testing condition, its stress rupture property at 1100 ℃/100 MPa is clearly improved, compared with900 ℃/445 MPa. The evident stress rupture anisotropy at 900 ℃/445 MPa is mainly attributed to the distinctive movement way of dislocations in each oriented sample. Whereas, at 1100 ℃/100 MPa, together with the individual dislocation configuration, the evolution of γ/γ′ microstructure in each orientation also plays a key role in the apparent stress rupture anisotropy.