摘 要：Mechanical behaviors of UHTCC after freezing and thawing were investigated,and compared with those of steel fiber reinforced concrete（SFRC）,air-entrained concrete（AEC） and ordinary concrete（OC）.Four point bending tests had been applied after different freezing-thawing cycles（0,50,100,150,200 and 300 cycles,respectively）.The results showed that residual flexural strength of UHTCC after 300 freezing-thawing cycles was 10.62 MPa（70% of no freezing thawing ones）,while 1.58 MPa（17% of no freezing thawing ones） for SFRC.Flexural toughness of UHTCC decreased by 17%,while 70% for SFRC comparatively.It has been demonstrated experimentally that UHTCC without any air-entraining agent could resist freezing-thawing and retain its high toughness characteristic in cold environment.Consequently,UHTCC could be put into practice for new-built or retrofit of infrastructures in cold regions.
徐世烺
The State Key Laboratory of Coastal and Offshore Engineering,Dalian University of Technology
摘 要：Mechanical behaviors of UHTCC after freezing and thawing were investigated,and compared with those of steel fiber reinforced concrete（SFRC）,air-entrained concrete（AEC） and ordinary concrete（OC）.Four point bending tests had been applied after different freezing-thawing cycles（0,50,100,150,200 and 300 cycles,respectively）.The results showed that residual flexural strength of UHTCC after 300 freezing-thawing cycles was 10.62 MPa（70% of no freezing thawing ones）,while 1.58 MPa（17% of no freezing thawing ones） for SFRC.Flexural toughness of UHTCC decreased by 17%,while 70% for SFRC comparatively.It has been demonstrated experimentally that UHTCC without any air-entraining agent could resist freezing-thawing and retain its high toughness characteristic in cold environment.Consequently,UHTCC could be put into practice for new-built or retrofit of infrastructures in cold regions.
关键词：