快速凝固耐热铝合金粉末脱气研究^①

来源期刊：中国有色金属学报1996年第4期

论文作者：黎文献 王维 肖于德 李松瑞

文章页码：135 - 138

关键词：快速凝固； 耐热铝合金； 真空除气

Key words：rapid solidification;　elevated temperature aluminum alloy;　vacuum degassing

摘    要：描述了FVS0812合金粉末压坯在整个脱气过程中温度—脱气量关系，得出700 K左右为该合金最佳脱气温度。借助X射线光电子能谱(XPS)对比分析压坯在真空加热除气与空气中加热后粉末表面氧化膜微观结构的不同，发现脱气者较未脱气者氧化膜薄30%以上，Fe、V等元素只分布在氧化膜内层。

Abstract: The degassing process of the powder blank of FVS0812 alloy was studied, and the relation between temperature and volume of degassing was described. The best degassing temperature was about 700K. The microstructure of the oxide film on the blank after vacuum heat-degassing was compared with that after heating in air through XPS. The results showed that the oxide film of powder after vacuum heat-degassing was 30% thinner than that after heating in air. The elements of Fe, V etc were only distributed inside the oxide film.