Citric Gel Synthesis and Luminescent Properties of Ce3+-Activated SrGa2O4 Phosphor
来源期刊：Journal of Rare Earths2007年第3期
论文作者：乔彬 唐子龙 张中太 陈雷
文章页码：286 - 290
摘 要：Ce3+-activated SrGa2O4 phosphor was synthesized by a method of citric gel,wherein citric acid served as a chelate agent,and the as-synthesized powder was calcined in a slightly reduced ambient.The crystallization characteristics of the sample varied with the calcining temperature.Compared with the phosphor prepared by the solid-state reaction,the phosphor synthesized by citric gel was calcined at a relatively lower temperature.Consequently,the volatilization of Ga2O3 during high-temperature calcining process was avoided.The typical double-peak emission of Ce3+ originated from 2D（5d）→4F5/2（4f）,and 2D（5d）→4F7/2（4f）was observed,and the intrinsic emission of SrGa2O4 host was much restricted.The emission intensity varied with the calcining temperature because the different crystallinity and the optimal concentration of Ce-dopant was determined at 3%.
乔彬，唐子龙，张中太，陈雷
摘 要：Ce3+-activated SrGa2O4 phosphor was synthesized by a method of citric gel,wherein citric acid served as a chelate agent,and the as-synthesized powder was calcined in a slightly reduced ambient.The crystallization characteristics of the sample varied with the calcining temperature.Compared with the phosphor prepared by the solid-state reaction,the phosphor synthesized by citric gel was calcined at a relatively lower temperature.Consequently,the volatilization of Ga2O3 during high-temperature calcining process was avoided.The typical double-peak emission of Ce3+ originated from 2D（5d）→4F5/2（4f）,and 2D（5d）→4F7/2（4f）was observed,and the intrinsic emission of SrGa2O4 host was much restricted.The emission intensity varied with the calcining temperature because the different crystallinity and the optimal concentration of Ce-dopant was determined at 3%.
关键词：