Electrochemical behavior of Y(Ⅲ) and preparation of Y-Ni intermetallic compounds in molten LiCl-KCl salts
来源期刊:JOURNAL OF RARE EARTHS2017年第1期
论文作者:韩伟 赵强 王季 李梅 刘文凯 张密林 杨晓光 孙杨
文章页码:90 - 97
摘 要:The work concerned the electrochemical behaviors of Y(Ⅲ) on W and Ni electrodes in molten LiCl-KCl salts by a series of electrochemical techniques. The electrochemical reaction of Y(Ⅲ) to Y(0) proceeded in a one-step reduction process with the exchange of three electrons, Y(Ⅲ)+3e–→Y(0). Compared with the cyclic voltammogram and square wave voltammogram obtained on W electrode, the reduction potential of Y(Ⅲ) on Ni electrode was observed at less negative potential than the one of Y(Ⅲ) to give pure Y metal on W electrode, which revealed the occurrence of underpotential deposition of Y(Ⅲ) on Ni electrode. Electromotive force(emf) measurements were performed to calculate the relative partial molar Gibbs energies and activities of Y in Y-Ni alloys. The standard Gibbs energies of formation for different Y-Ni intermetallic compounds were also estimated. The different Y-Ni alloys were formed by potentiostatic electrolysis at different potentials and characterized by X-ray diffraction(XRD), scanning electron microscopy(SEM), and energy dispersive spectrometry(EDS). It was found that four intermetallic compounds, YNi5, Y2Ni7, YNi3 and YNi2, were selectively produced by controlling applied potential.
韩伟,赵强,王季,李梅,刘文凯,张密林,杨晓光,孙杨
Key Laboratory of Superlight Materials and Surface Technology,Ministry of Education,College of Materials Science and Chemical Engineering,Harbin Engineering University
摘 要:The work concerned the electrochemical behaviors of Y(Ⅲ) on W and Ni electrodes in molten LiCl-KCl salts by a series of electrochemical techniques. The electrochemical reaction of Y(Ⅲ) to Y(0) proceeded in a one-step reduction process with the exchange of three electrons, Y(Ⅲ)+3e–→Y(0). Compared with the cyclic voltammogram and square wave voltammogram obtained on W electrode, the reduction potential of Y(Ⅲ) on Ni electrode was observed at less negative potential than the one of Y(Ⅲ) to give pure Y metal on W electrode, which revealed the occurrence of underpotential deposition of Y(Ⅲ) on Ni electrode. Electromotive force(emf) measurements were performed to calculate the relative partial molar Gibbs energies and activities of Y in Y-Ni alloys. The standard Gibbs energies of formation for different Y-Ni intermetallic compounds were also estimated. The different Y-Ni alloys were formed by potentiostatic electrolysis at different potentials and characterized by X-ray diffraction(XRD), scanning electron microscopy(SEM), and energy dispersive spectrometry(EDS). It was found that four intermetallic compounds, YNi5, Y2Ni7, YNi3 and YNi2, were selectively produced by controlling applied potential.
关键词: