Properties of high calcium fly ash geopolymer pastes with Portland cement as an additive

来源期刊:International Journal of Minerals Metallurgy and Materials2013年第2期

论文作者:Tanakorn Phoo-ngernkham Prinya Chindaprasirt Vanchai Sata Saengsuree Pangdaeng Theerawat Sinsiri

文章页码:214 - 220

摘    要:The effect of Portland cement(OPC) addition on the properties of high calcium fly ash geopolymer pastes was investigated in the paper.OPC partially replaced fly ash(FA) at the dosages of 0,5%,10%,and 15% by mass of binder.Sodium silicate(Na2SiO3) and sodium hydroxide(NaOH) solutions were used as the liquid portion in the mixture:NaOH 10 mol/L,Na2SiO3/NaOH with a mass ratio of 2.0,and alkaline liquid/binder(L/B) with a mass ratio of 0.6.The curing at 60 C for 24 h was used to accelerate the geopolymerization.The setting time of all fresh pastes,porosity,and compressive strength of the pastes at the stages of 1,7,28,and 90 d were tested.The elastic modulus and strain capacity of the pastes at the stage of 7 d were determined.It is revealed that the use of OPC as an additive to replace part of FA results in the decreases in the setting time,porosity,and strain capacity of the paste specimens,while the compressive strength and elastic modulus seem to increase.

详情信息展示

Properties of high calcium fly ash geopolymer pastes with Portland cement as an additive

Tanakorn Phoo-ngernkham1,Prinya Chindaprasirt1,Vanchai Sata1,Saengsuree Pangdaeng1,Theerawat Sinsiri2

1. Sustainable Infrastructure Research and Development Center,Department of Civil Engineering,Faculty of Engineering,Khon Kaen University2. School of Civil Engineering,Institute of Engineering,Suranaree University of Technology

摘 要:The effect of Portland cement(OPC) addition on the properties of high calcium fly ash geopolymer pastes was investigated in the paper.OPC partially replaced fly ash(FA) at the dosages of 0,5%,10%,and 15% by mass of binder.Sodium silicate(Na2SiO3) and sodium hydroxide(NaOH) solutions were used as the liquid portion in the mixture:NaOH 10 mol/L,Na2SiO3/NaOH with a mass ratio of 2.0,and alkaline liquid/binder(L/B) with a mass ratio of 0.6.The curing at 60 C for 24 h was used to accelerate the geopolymerization.The setting time of all fresh pastes,porosity,and compressive strength of the pastes at the stages of 1,7,28,and 90 d were tested.The elastic modulus and strain capacity of the pastes at the stage of 7 d were determined.It is revealed that the use of OPC as an additive to replace part of FA results in the decreases in the setting time,porosity,and strain capacity of the paste specimens,while the compressive strength and elastic modulus seem to increase.

关键词:

<上一页 1 下一页 >

有色金属在线官网  |   会议  |   在线投稿  |   购买纸书  |   科技图书馆

中南大学出版社 技术支持 版权声明   电话:0731-88830515 88830516   传真:0731-88710482   Email:administrator@cnnmol.com

互联网出版许可证:(署)网出证(京)字第342号   京ICP备17050991号-6      京公网安备11010802042557号