Preparation and structure of microarc oxidation ceramic coatings containing ZrO2 grown on LY12 Al alloy
来源期刊：Rare Metals2008年第1期
论文作者：WU Zhendonga,b,YAO Zhongpinga,and JIANG Zhaohuaaa Department of Applied Chemistry,Harbin Institute of Technology,Harbin ,China b Department of Applied Chemistry,Baicheng Normal College,Baicheng ,China
文章页码：55 - 58
摘 要：Ceramic coatings containing ZrO2 were prepared in situ on LY12 aluminum alloy by microarc oxidation（MAO） in the mixed solution of zirconate and phosphate solution.The phase composition and morphology of the coatings were studied by XRD and SEM,respectively.The growing mechanism of ceramic coatings was discussed in a preliminary manner.The results show that with an increase in MAO time,the compactness of the coating improved and the thickness increased.From the inner layer to the coating surface,the content of Zr increased,while the content of Al decreased.In addition,the coating was composed of m-ZrO2,t-ZrO2,and a little amount of γ-Al2O3.With an increase in reaction time,the relative content of t-ZrO2 within the coating sharply decreased while the relative content of m-ZrO2 sharply increased,and then both generally kept at a constant level after 60 min.
WU Zhendonga,b,YAO Zhongpinga,and JIANG Zhaohuaaa Department of Applied Chemistry,Harbin Institute of Technology,Harbin 150001,China b Department of Applied Chemistry,Baicheng Normal College,Baicheng 137000,China
摘 要：Ceramic coatings containing ZrO2 were prepared in situ on LY12 aluminum alloy by microarc oxidation（MAO） in the mixed solution of zirconate and phosphate solution.The phase composition and morphology of the coatings were studied by XRD and SEM,respectively.The growing mechanism of ceramic coatings was discussed in a preliminary manner.The results show that with an increase in MAO time,the compactness of the coating improved and the thickness increased.From the inner layer to the coating surface,the content of Zr increased,while the content of Al decreased.In addition,the coating was composed of m-ZrO2,t-ZrO2,and a little amount of γ-Al2O3.With an increase in reaction time,the relative content of t-ZrO2 within the coating sharply decreased while the relative content of m-ZrO2 sharply increased,and then both generally kept at a constant level after 60 min.
关键词：