Rational design of monovalent ions (Li,Na,K) co-doped ZnAl2O4:Eu3+ nanocrystals enabling versatile robust latent fingerprint visualization

来源期刊:JOURNAL OF RARE EARTHS2019年第7期

论文作者:F.Femila Komahal H.Nagabhushana R.B.Basavaraj B.Daruka Prasad

文章页码:699 - 705

摘    要:Alkali metal ions(M+ = Na+,Li+,K+) co-doped ZnAl2O4:Eu3+(5 mol%)(ZAE) nanopowders(NPs) were prepared via solution combustion route using Mimosa pudica(MP) leaves extract as a fuel. PXRD results of co-doped samples enhance the crystallinity and grain growth. Photoluminescence(PL) of the prepared ZAE and ZAE:M+(M+ = Na+, Li+, K+) NPs shows intense emission peaks in the range of 550-750 nm and ascribed to 5D07FJ(J=0-4) transitions of Eu3+ ions, respectively. A 2-fold enhancement in PL intensity was observed in Li+ co-doped samples. The optimized ZnAl2O4:Eu3+(5 mol%), Li+(1 wt%)(ZAEL)NPs were used to visualize LFPs on various porous, semi-porous and non-porous surfaces through robust powder dusting technique. The visualized latent fingerprints(LFPs) reveal well defined level 1-3 ridge characteristics under several tests such as fingerprint aging and fresh water treatment for various time durations. The obtained results clearly evidence that the prepared NPs are quite useful for multifunctional applications such as advanced forensic and solid state lightning.

详情信息展示

Rational design of monovalent ions (Li,Na,K) co-doped ZnAl2O4:Eu3+ nanocrystals enabling versatile robust latent fingerprint visualization

F.Femila Komahal1,H.Nagabhushana1,R.B.Basavaraj1,B.Daruka Prasad5

1. C.N.R.Rao Centre for Advanced Materials Research, Tumkur University5. Department of Physics, B.M.S.Institute of Technology, Visveswaraya Technological University

摘 要:Alkali metal ions(M+ = Na+,Li+,K+) co-doped ZnAl2O4:Eu3+(5 mol%)(ZAE) nanopowders(NPs) were prepared via solution combustion route using Mimosa pudica(MP) leaves extract as a fuel. PXRD results of co-doped samples enhance the crystallinity and grain growth. Photoluminescence(PL) of the prepared ZAE and ZAE:M+(M+ = Na+, Li+, K+) NPs shows intense emission peaks in the range of 550-750 nm and ascribed to 5D07FJ(J=0-4) transitions of Eu3+ ions, respectively. A 2-fold enhancement in PL intensity was observed in Li+ co-doped samples. The optimized ZnAl2O4:Eu3+(5 mol%), Li+(1 wt%)(ZAEL)NPs were used to visualize LFPs on various porous, semi-porous and non-porous surfaces through robust powder dusting technique. The visualized latent fingerprints(LFPs) reveal well defined level 1-3 ridge characteristics under several tests such as fingerprint aging and fresh water treatment for various time durations. The obtained results clearly evidence that the prepared NPs are quite useful for multifunctional applications such as advanced forensic and solid state lightning.

关键词:

<上一页 1 下一页 >

有色金属在线官网  |   会议  |   在线投稿  |   购买纸书  |   科技图书馆

中南大学出版社 技术支持 版权声明   电话:0731-88830515 88830516   传真:0731-88710482   Email:administrator@cnnmol.com

互联网出版许可证:(署)网出证(京)字第342号   京ICP备17050991号-6      京公网安备11010802042557号