Hydrogen storage properties of nanocomposite Mg-Ni-MnO2 made by mechanical milling

来源期刊:中国有色金属学报(英文版)2002年第2期

论文作者:王尔德 于振兴 刘祖岩

文章页码:227 - 232

Key words:mechanical milling; nanocomposite Mg-Ni-MnO2; hydrogen storage materials

Abstract: The hydrogen storage properties of the nanocomposite Mg95Ni3(MnO2)2 (mass fraction, %) were studied. The temperature changes in hydriding/dehydriding process were investigated. The nanocomposite was fabricated by ball milling process of mixed elemental Mg, Ni and oxide maganese MnO2 under hydrogen pressure (approximately 0.6MPa). The hydrogen absorption and desorption properties of the samples milled for various times were investigated. A remarkable enhancement of hydrogen absorption kinetics and low operational desorption temperature have been found after the sample milled for over 57h. For example, this nanocomposite can absorb hydrogen more than 6.0% (mass fraction) in 60s at 200℃ under 2.0MPa, and desorption capacity also exceeds 6.0% (mass fraction) in 400s at 310℃ under 0.1MPa. The storage properties of samples milled for various times were studied and the kinetics of the samples were analyzed.

详情信息展示

<上一页 1 下一页 >

有色金属在线官网  |   会议  |   在线投稿  |   购买纸书  |   科技图书馆

中南大学出版社 技术支持 版权声明   电话:0731-88830515 88830516   传真:0731-88710482   Email:administrator@cnnmol.com

互联网出版许可证:(署)网出证(京)字第342号   京ICP备17050991号-6      京公网安备11010802042557号