Bacteria Adherence Properties of Nitrided Layer on Ti6Al4V by the Plasma Nitriding Technique
来源期刊:Journal Of Wuhan University Of Technology Materials Science Edition2013年第6期
论文作者:FAN Ailan ZHANG Huiqiao MA Yong ZHANG Xiangyu ZHANG Jianqiang TANG Bin
文章页码:1223 - 1226
摘 要:The nitrided layer on Ti6Al4V substrate was prepared by the plasma nitriding technique. The sample was characterized by X-ray diffraction(XRD), glow discharge optical emission spectroscopy(GDOES), X-ray photoelectron spectroscopy(XPS), and rough-meter. X- ray diffraction analysis reveals that TiN, Ti 2 N and Ti phase exist in the nitrided layer subsurface. GDOES analysis shows the thickness of the nitrided layer is about 3 μm. XPS analysis shows that there is higher N, lower Al and lower V in the nitrided layer surface than in the Ti6Al4V surface. Rough-meter analysis results show the roughness of the nitrided layer is greater than that of Ti6Al4V alloy base. The bacteria adherence property of the nitrided layer on Ti6Al4V substrate on the Streptococcus mutans was investigated and compared with that of Ti6Al4V alloy by fluorescence microscope. It shows that the nitrided layer inhibits the bacteria adherence.
FAN Ailan1,ZHANG Huiqiao1,MA Yong1,ZHANG Xiangyu1,ZHANG Jianqiang2,3,TANG Bin1
1. Research Institute of Surface Engineering,Taiyuan University of Technology2. College of Environmental Engineering,Taiyuan University of Technology3. Department of Architectural Engineering,Shanxi Polytechnic College
摘 要:The nitrided layer on Ti6Al4V substrate was prepared by the plasma nitriding technique. The sample was characterized by X-ray diffraction(XRD), glow discharge optical emission spectroscopy(GDOES), X-ray photoelectron spectroscopy(XPS), and rough-meter. X- ray diffraction analysis reveals that TiN, Ti 2 N and Ti phase exist in the nitrided layer subsurface. GDOES analysis shows the thickness of the nitrided layer is about 3 μm. XPS analysis shows that there is higher N, lower Al and lower V in the nitrided layer surface than in the Ti6Al4V surface. Rough-meter analysis results show the roughness of the nitrided layer is greater than that of Ti6Al4V alloy base. The bacteria adherence property of the nitrided layer on Ti6Al4V substrate on the Streptococcus mutans was investigated and compared with that of Ti6Al4V alloy by fluorescence microscope. It shows that the nitrided layer inhibits the bacteria adherence.