Synthesis,structure and near-infrared luminescence of a new 2D praseodymium(Ⅲ) coordination polymer
来源期刊:JOURNAL OF RARE EARTHS2011年第11期
论文作者:刘光祥 周宏 任小明
文章页码:1100 - 1104
摘 要:A novel coordination polymer,[Pr2(BIPA)3(H2O)2].2H2O(1)(H2BIPA=5-bromoisophthalic acid),was prepared by hydrothermal synthesis and characterized by IR spectroscopy,elemental analysis and single-crystal X-ray diffraction.The crystal was of monoclinic system,space group C2/c,with a=1.98037(14),b=1.44189(14),c=2.15281(18) nm,β=95.220(2)°,V=6.1218(9) nm3,C24H17Br3O16Pr2,Mr=1082.93,Dc= 2.350 g/cm3,F(000)=4096,μ=7.136 mm-1 and Z=8.The final R1=0.0608 and wR2=0.1371 for 5624 observed reflections(I>2σ(I)).Complex 1 featured an interesting 2D layer containing {Pr2(CO2)3}n right-handed and left-handed helical chains.Furthermore,hydrogen bonds linked the adjacent 2D layers to form a 3D supramolecular framework.Moreover,the near-infrared luminescent properties of 1 were also investigated in the solid state.
刘光祥1,周宏1,任小明2
1. Department of Chemistry,Nanjing Xiaozhuang University2. College of Science,Nanjing University of Technology
摘 要:A novel coordination polymer,[Pr2(BIPA)3(H2O)2].2H2O(1)(H2BIPA=5-bromoisophthalic acid),was prepared by hydrothermal synthesis and characterized by IR spectroscopy,elemental analysis and single-crystal X-ray diffraction.The crystal was of monoclinic system,space group C2/c,with a=1.98037(14),b=1.44189(14),c=2.15281(18) nm,β=95.220(2)°,V=6.1218(9) nm3,C24H17Br3O16Pr2,Mr=1082.93,Dc= 2.350 g/cm3,F(000)=4096,μ=7.136 mm-1 and Z=8.The final R1=0.0608 and wR2=0.1371 for 5624 observed reflections(I>2σ(I)).Complex 1 featured an interesting 2D layer containing {Pr2(CO2)3}n right-handed and left-handed helical chains.Furthermore,hydrogen bonds linked the adjacent 2D layers to form a 3D supramolecular framework.Moreover,the near-infrared luminescent properties of 1 were also investigated in the solid state.
关键词: