One-pot Synthesis of Hollow Octahedral Cu2O Nanostructures at Room Temperature
来源期刊：Journal Of Wuhan University Of Technology Materials Science Edition2013年第1期
论文作者：雷丽文 ZHANG Qi ZHANG Yu ZHANG Jinyong WANG Hao FU Zhengyi
文章页码：40 - 43
摘 要：Homogeneous hollow Cu2O octahedral nanostructures have been fabricated by a facile one-pot reduction reaction at room temperature. The microscope analysis revealed that the edges of as-prepared hollow structures were around 200 nm with a wall thickness of about 20 nm. To investigate the influence factors and formation mechanism of the hollow octahedral structure, samples subjected to different reaction conditions were studies. The results showed that the morphology and structures of Cu2O particles were greatly affected by the concentration of pH value of the reaction environment and the reaction time. Ostwald ripening process is proposed to explain the growth mechanism of the hollow octahedral nanostructures.
雷丽文1,2，ZHANG Qi2，ZHANG Yu2，ZHANG Jinyong1，WANG Hao1，FU Zhengyi1
1. State Key Lab of Advanced Technology for Materials Synthesis and Processing，Wuhan University of Technology2. School of Materials Science and Engineering, Wuhan University of Technology
摘 要：Homogeneous hollow Cu2O octahedral nanostructures have been fabricated by a facile one-pot reduction reaction at room temperature. The microscope analysis revealed that the edges of as-prepared hollow structures were around 200 nm with a wall thickness of about 20 nm. To investigate the influence factors and formation mechanism of the hollow octahedral structure, samples subjected to different reaction conditions were studies. The results showed that the morphology and structures of Cu2O particles were greatly affected by the concentration of pH value of the reaction environment and the reaction time. Ostwald ripening process is proposed to explain the growth mechanism of the hollow octahedral nanostructures.