Behavior of fluxed lime iron oxide pellets in hot metal bath during melting and refining
来源期刊：International Journal of Minerals Metallurgy and Materials2013年第4期
论文作者：J. Pal S. Ghorai M. C. Goswami D. Ghosh D. Bandyopadhyay S. Ghosh
文章页码：329 - 337
摘 要：Lump lime as a flux material in a basic oxygen furnace （BOF） often creates problems in operation due to its high melting point, poor dissolution property, hygroscopic nature, and fines generation tendency. To alleviate these problems, fluxed lime iron oxide pellets （FLIP） containing 30% CaO were developed in this study using waste iron oxide fines and lime. The suitable handling strengths of the pellet （crushing strength: 300N; drop strength: 130 times） of FLIP were developed by treating with CO2 or industrial waste gas at room temperature, while no separate binders were used. When the pellet was added into hot metal bath （carbon-containing molten iron）, it was decomposed, melted, and transformed to produce low melting oxidizing slag, because it is a combination of main CaO and Fe2O3 . This slag is suitable for facilitating P and C removal in refining. Furthermore, the pellet enhances waste utilization and use of CO2 in waste gas. In this article, emphasis is given on studying the behavior of these pellets in hot metal bath during melting and refining along with thermodynamics and kinetics analysis. The observed behaviors of the pellet in hot metal bath confirm that it is suitable and beneficial for use in BOF and replaces lump lime.
J. Pal1，S. Ghorai1，M. C. Goswami1，D. Ghosh2，D. Bandyopadhyay1，S. Ghosh1
1. CSIR-National Metallurgical Laboratory2. Department of Metallurgical and Material Engineering, Jadavpur University
摘 要：Lump lime as a flux material in a basic oxygen furnace （BOF） often creates problems in operation due to its high melting point, poor dissolution property, hygroscopic nature, and fines generation tendency. To alleviate these problems, fluxed lime iron oxide pellets （FLIP） containing 30% CaO were developed in this study using waste iron oxide fines and lime. The suitable handling strengths of the pellet （crushing strength: 300N; drop strength: 130 times） of FLIP were developed by treating with CO2 or industrial waste gas at room temperature, while no separate binders were used. When the pellet was added into hot metal bath （carbon-containing molten iron）, it was decomposed, melted, and transformed to produce low melting oxidizing slag, because it is a combination of main CaO and Fe2O3 . This slag is suitable for facilitating P and C removal in refining. Furthermore, the pellet enhances waste utilization and use of CO2 in waste gas. In this article, emphasis is given on studying the behavior of these pellets in hot metal bath during melting and refining along with thermodynamics and kinetics analysis. The observed behaviors of the pellet in hot metal bath confirm that it is suitable and beneficial for use in BOF and replaces lump lime.