Influence of La2O3 addition on nano indentation hardness and residual stress of Stellite 6 coating prepared by plasma cladding
来源期刊:JOURNAL OF RARE EARTHS2018年第8期
论文作者:Yongchao Fang Xiufang Cui Zhaobing Cai Chang Wang Guo Jin
文章页码:873 - 878
摘 要:One of the problems limiting the application of Stellite 6 coating is the residual stress resulting in cracks in the coating easily. In order to reduce the residual stress and increase the nano-indentation hardness,La2 O3 was added to Stellite 6 coating in this study, and the influence on the microstructure, nano indentation hardness and residual stress of the coatings were investigated by scanning electron microscopy(SEM) with energy dispersive spectrum(EDS), X-ray diffraction(XRD) and nano-indentation tester. Results indicate that the addition of La2 O3 leads to the phenomenon that the dendrite is partly transformed into the equiaxed grain, which results in the grain refinement. The nano-indentation hardness of coatings is improved, which is attributed to the fine-grain strengthening and dispersion strengthening effect of La2 O3. With the addition of La2 O3, the residual stress in coatings is decreased significantly. Especially, when the content of La2 O3 is 0.8 wt%, the nano indentation hardness increases by 1.31 times and residual stress decreases to 20 percent, compared with coating without La2 O3.
Yongchao Fang,Xiufang Cui,Zhaobing Cai,Chang Wang,Guo Jin
Institute of Surface/Interface Science and Technology, Key Laboratory of Superlight Material and Surface Technology of Ministry of Education, College of Material Science and Chemical Engineering, Harbin Engineering University
摘 要:One of the problems limiting the application of Stellite 6 coating is the residual stress resulting in cracks in the coating easily. In order to reduce the residual stress and increase the nano-indentation hardness,La2 O3 was added to Stellite 6 coating in this study, and the influence on the microstructure, nano indentation hardness and residual stress of the coatings were investigated by scanning electron microscopy(SEM) with energy dispersive spectrum(EDS), X-ray diffraction(XRD) and nano-indentation tester. Results indicate that the addition of La2 O3 leads to the phenomenon that the dendrite is partly transformed into the equiaxed grain, which results in the grain refinement. The nano-indentation hardness of coatings is improved, which is attributed to the fine-grain strengthening and dispersion strengthening effect of La2 O3. With the addition of La2 O3, the residual stress in coatings is decreased significantly. Especially, when the content of La2 O3 is 0.8 wt%, the nano indentation hardness increases by 1.31 times and residual stress decreases to 20 percent, compared with coating without La2 O3.