Microwave assisted synthesis & properties of nano HA-TCP biphasic calcium phosphate
来源期刊:International Journal of Minerals Metallurgy and Materials2012年第5期
论文作者:E.Ghomash Pasand A.Nemati M.Solati-Hashjin K.Arzani A.Farzadi
文章页码:441 - 445
摘 要:Biphasic calcium phosphate(BCP) nanopowders were synthesized by using microwave and non-microwave irradiation assisted processes.The synthesized powders were pressed under a pressure of 90 MPa,and then were sintered at 1000-1200°C for 1 h.The mechanical properties of the samples were investigated.The formed phases and microstructures were characterized by X-ray diffraction(XRD) and scanning electron microscopy(SEM).The results showed that the synthesis time was shorter,along with a more homogeneous microstructure,when the microwave irradiation assisted method was applied.The compression strength and the Young’s modulus of the samples synthesized with microwave irradiation were about 60 MPa and 3 GPa,but those of the samples synthesized without microwave irradiation were about 30 MPa and 2 GPa,respectively.XRD patterns of the microwave irradiation assisted and non-microwave irradiation assisted nanopowders showed the coexistence of hydroxyapatite(HA) and tricalcium phosphate(TCP) phases in the system.
E.Ghomash Pasand1,A.Nemati1,M.Solati-Hashjin2,K.Arzani1,A.Farzadi2
1. Department of Materials Engineering,Science and Research Branch,Islamic Azad University,Tehran 1477893855,Iran2. Department of Biomedical Engineering,Amirkabir University of Technology,Tehran 158754413,Iran
摘 要:Biphasic calcium phosphate(BCP) nanopowders were synthesized by using microwave and non-microwave irradiation assisted processes.The synthesized powders were pressed under a pressure of 90 MPa,and then were sintered at 1000-1200°C for 1 h.The mechanical properties of the samples were investigated.The formed phases and microstructures were characterized by X-ray diffraction(XRD) and scanning electron microscopy(SEM).The results showed that the synthesis time was shorter,along with a more homogeneous microstructure,when the microwave irradiation assisted method was applied.The compression strength and the Young’s modulus of the samples synthesized with microwave irradiation were about 60 MPa and 3 GPa,but those of the samples synthesized without microwave irradiation were about 30 MPa and 2 GPa,respectively.XRD patterns of the microwave irradiation assisted and non-microwave irradiation assisted nanopowders showed the coexistence of hydroxyapatite(HA) and tricalcium phosphate(TCP) phases in the system.