Synthesis and optical properties of turquoise-and green-colored brownmilleritetype Ba2In2-x-yMnxAlyO5+x codoped with manganese and aluminum
来源期刊:International Journal of Minerals Metallurgy and Materials2016年第11期
论文作者:Peng Jiang Wen-hui Yang Yun-cheng Zhou Jian-lei Kuang Yong Li Ting Xiao
文章页码:1346 - 1351
摘 要:Brownmillerite-type oxides Ba2In2-x-yMnxAlyO5+x(0 ≤ x ≤ 0.6, 0 ≤ y ≤ 0.5) were prepared at 1300°C through solid-state reaction. X-ray diffraction(XRD) analysis showed that the structure symmetry evolved from orthorhombic to cubic with increasing Mn and Al contents. When y was greater than 0.3, peaks associated with small amounts of BaAl2O4 and Ba2InAlO5 impurities were observed in the XRD patterns. When substituted with a small amount of Mn(x ≤ 0.3), the Ba2In2-x-yMnxAlyO5+x samples exhibited an intense turquoise color. The color changed to green and dark-green with increasing Mn concentration. UV–vis absorbance spectra revealed that the color changed only slightly upon Al doping. The valence state of Mn ions in Ba2In2-x-yMnxAlyO5+x was confirmed to be +5 on the basis of X-ray photoelectron spectroscopic analysis. According to this analysis, the intense turquoise color of the Ba2In2-x-yMnxAlyO5+x samples is rooted in the existence of Mn5+; thus, the introduction of Al does not affect the optical properties of the compounds.
Peng Jiang,Wen-hui Yang,Yun-cheng Zhou,Jian-lei Kuang,Yong Li,Ting Xiao
School of Materials Science and Engineering,University of Science and Technology Beijing
摘 要:Brownmillerite-type oxides Ba2In2-x-yMnxAlyO5+x(0 ≤ x ≤ 0.6, 0 ≤ y ≤ 0.5) were prepared at 1300°C through solid-state reaction. X-ray diffraction(XRD) analysis showed that the structure symmetry evolved from orthorhombic to cubic with increasing Mn and Al contents. When y was greater than 0.3, peaks associated with small amounts of BaAl2O4 and Ba2InAlO5 impurities were observed in the XRD patterns. When substituted with a small amount of Mn(x ≤ 0.3), the Ba2In2-x-yMnxAlyO5+x samples exhibited an intense turquoise color. The color changed to green and dark-green with increasing Mn concentration. UV–vis absorbance spectra revealed that the color changed only slightly upon Al doping. The valence state of Mn ions in Ba2In2-x-yMnxAlyO5+x was confirmed to be +5 on the basis of X-ray photoelectron spectroscopic analysis. According to this analysis, the intense turquoise color of the Ba2In2-x-yMnxAlyO5+x samples is rooted in the existence of Mn5+; thus, the introduction of Al does not affect the optical properties of the compounds.