Effect of mischmetal on mechanical properties and microstructure of die-cast magnesium alloy AZ91D
来源期刊：JOURNAL OF RARE EARTHS2016年第7期
论文作者：徐玉磊 张奎 雷健
文章页码：742 - 746
摘 要：Effects of the mischmetal addition in range of 0.4 wt.% to 1.7 wt.% on the microstructure and mechanical properties of die-cast magnesium AZ91D were investigated to improve the elevated temperature mechanical properties of the alloy by scanning electron microscopy, transmission electron microscopy, X-ray diffraction and tensile tests. The results revealed that mechanical properties of die-cast magnesium alloy AZ91D-0.4%MM at 100 oC were near to those of die-cast magnesium alloy AZ91D. The ultimate tensile strength, 0.2% proof yield strength and elongation to failure of die-cast magnesium alloy AZ91D at 170 oC were 178, 129 MPa and 20%, respectively. In comparison, the ultimate tensile strength, 0.2% proof yield strength and elongation to failure of die-cast magnesium alloy AZ91D-0.4%MM at 170 oC reached to 206, 142 MPa and 26%, respectively increased by 15.7%, 10% and 30%. Proper addition of mischmetal could enhance the mechanical properties at an elevated temperature, which was attributed to the formation of Al-RE phases with high thermal stability. Hence sliding of grain boundaries and cracks could be effectively hindered by Al-RE phases.
徐玉磊1，张奎2，雷健3
1. School of Materials and Metallurgy, Inner Mongolia University of Science and Technology2. State Key Laboratory for Fabrication and Processing of Nonferrous Metals, General Research Institute for Nonferrous Metals3. Material Technology Institute of BVTC,DongFeng Motor Co.,Ltd.
摘 要：Effects of the mischmetal addition in range of 0.4 wt.% to 1.7 wt.% on the microstructure and mechanical properties of die-cast magnesium AZ91D were investigated to improve the elevated temperature mechanical properties of the alloy by scanning electron microscopy, transmission electron microscopy, X-ray diffraction and tensile tests. The results revealed that mechanical properties of die-cast magnesium alloy AZ91D-0.4%MM at 100 oC were near to those of die-cast magnesium alloy AZ91D. The ultimate tensile strength, 0.2% proof yield strength and elongation to failure of die-cast magnesium alloy AZ91D at 170 oC were 178, 129 MPa and 20%, respectively. In comparison, the ultimate tensile strength, 0.2% proof yield strength and elongation to failure of die-cast magnesium alloy AZ91D-0.4%MM at 170 oC reached to 206, 142 MPa and 26%, respectively increased by 15.7%, 10% and 30%. Proper addition of mischmetal could enhance the mechanical properties at an elevated temperature, which was attributed to the formation of Al-RE phases with high thermal stability. Hence sliding of grain boundaries and cracks could be effectively hindered by Al-RE phases.
关键词：