Corrosion Behavior of 304 Stainless Steel Exposed to a Simulated Salt Lake Atmosphere
来源期刊：Acta Metallurgica Sinica2020年第6期
论文作者：Mingxiao Guo Qi Yin Miaoran Liu Chen Pan Zhenyao Wang
文章页码：857 - 870
摘 要：The corrosion behavior of stainless steel exposed to a simulated salt lake atmosphere has been investigated by analyzing the evolution of surface morphologies and corrosion products, the initiation and development of pits, and the electrochemical characteristics. The results indicated that(Mg6Fe2（OH）16（CO3）（H2O）4.5)0.25, a layered double hydroxide, has been detected for the first time in the corrosion products formed on stainless steel exposed to a simulated salt lake atmosphere. The specimens exposed to MgCl2 deposit conditions were corroded more severely than those exposed to NaCl deposit conditions, which was attributed to the differences in the deliquescence relative humidity and efflorescence relative humidity values of MgCl2 and NaCl. In addition, a special corrosion morphology consisting of a concentric circle of yellowish material was observed on the specimens exposed to MgCl2 deposit conditions, which was attributed to the formation of Mg（OH）2, inhibiting the diffusion and migration of OH- ions to the anode region. The maximum pit depth followed a power function with respect to corrosion time. The corrosion mechanism of stainless steel exposed to a simulated salt lake atmosphere is also discussed.
Mingxiao Guo1,2，Qi Yin1,2，Miaoran Liu1,3，Chen Pan1，Zhenyao Wang1
1. Institute of Metal Research,Chinese Academy of Sciences2. School of Materials Science and Engineering,University of Science and Technology of China3. University of Chinese Academy of Sciences
摘 要：The corrosion behavior of stainless steel exposed to a simulated salt lake atmosphere has been investigated by analyzing the evolution of surface morphologies and corrosion products, the initiation and development of pits, and the electrochemical characteristics. The results indicated that(Mg6Fe2（OH）16（CO3）（H2O）4.5)0.25, a layered double hydroxide, has been detected for the first time in the corrosion products formed on stainless steel exposed to a simulated salt lake atmosphere. The specimens exposed to MgCl2 deposit conditions were corroded more severely than those exposed to NaCl deposit conditions, which was attributed to the differences in the deliquescence relative humidity and efflorescence relative humidity values of MgCl2 and NaCl. In addition, a special corrosion morphology consisting of a concentric circle of yellowish material was observed on the specimens exposed to MgCl2 deposit conditions, which was attributed to the formation of Mg（OH）2, inhibiting the diffusion and migration of OH- ions to the anode region. The maximum pit depth followed a power function with respect to corrosion time. The corrosion mechanism of stainless steel exposed to a simulated salt lake atmosphere is also discussed.
关键词：