Effects of W Addition on the Electrochemical Behaviour and Passive Film Properties of Fe-Based Amorphous Alloys in Acetic Acid Solution
来源期刊:Acta Metallurgica Sinica2018年第10期
论文作者:Dan-Dan Liang Xian-Shun Wei Chun-Tao Chang Jia-Wei Li Yong Wang Xin-Min Wang Jun Shen
文章页码:1098 - 1108
摘 要:The electrochemical behaviour and passive film properties of Fe–Cr–Mo–W–C–B–Y amorphous alloys in acetic acid solution were investigated. The potentiodynamic polarisation and Nyquist curves demonstrated that W addition significantly enhanced the corrosion resistance. Mott–Schottky plots and angle-resolved X-ray photoelectron spectra indicated that passive films with different W contents exhibited dipolar(p–n) semiconducting characteristics separated by flat-band potentials. The outer and inner oxide layers of the passive films were modified by reducing the acceptor and donor densities. Moreover, W addition favoured the formation of a thicker and more stable passive film to inhibit the dissolution of alloy elements.
Dan-Dan Liang1,Xian-Shun Wei1,Chun-Tao Chang2,3,Jia-Wei Li2,3,Yong Wang4,Xin-Min Wang2,3,Jun Shen1
1. School of Materials Science and Engineering, Tongji University2. Key Laboratory of Magnetic Materials and Devices, Ningbo Institute of Materials Technology and Engineering, Chinese Academy of Sciences3. Zhejiang Province Key Laboratory of Magnetic Materials and Application Technology, Ningbo Institute of Materials Technology and Engineering, Chinese Academy of Sciences4. School of Mechanical Science and Engineering, Northeast Petroleum University
摘 要:The electrochemical behaviour and passive film properties of Fe–Cr–Mo–W–C–B–Y amorphous alloys in acetic acid solution were investigated. The potentiodynamic polarisation and Nyquist curves demonstrated that W addition significantly enhanced the corrosion resistance. Mott–Schottky plots and angle-resolved X-ray photoelectron spectra indicated that passive films with different W contents exhibited dipolar(p–n) semiconducting characteristics separated by flat-band potentials. The outer and inner oxide layers of the passive films were modified by reducing the acceptor and donor densities. Moreover, W addition favoured the formation of a thicker and more stable passive film to inhibit the dissolution of alloy elements.