Durability experiment on anti-electron-bombardment of RE2O3-Mo secondary emission material

来源期刊:中国有色金属学报(英文版)2004年第2期

论文作者:杨飒 王金淑 周美玲 高玉娟 李洪义

文章页码:274 - 277

Key words:rare earth oxide; molybdenum; anti-electron-bombardment property; secondary emission

Abstract: A durability test to determine anti-bombardment sensitivity of multi- RE2O3-Mo secondary emission material was carried out and the variation of maximum secondary emission coefficient (δmax) was monitored at regular intervals. After the experiment, the cathode was analyzed with SEM, EDS and XRD techniques. The results show thatδmaxof multi-RE2O3-Mo cermets cathode heated to 1 100℃under electron bombardment of 300 W/cm2reaches the peak of 3.35 at 200 h. After 500 h of bombardment, the maximum secondary-electron-yield curve stabilizes. Theδmaxvalue of the cathode remains at about 2.5 after 1 000 h and represents a good anti-bombardment property. The highδmaxvalue of the cathode is related with formation of an enriched Y2O3layer on the surface under high temperature and with the amount ofLa2O3 particles in the shape of nanometer distributed on the surface. Under the experimental conditions, the drop ofδmax value may be caused by the reduction of La2O3content and the porous layer resulted from evaporation of MoO2, which is formed when Mo at the surface is oxidized.

详情信息展示

 

<上一页 1 下一页 >

有色金属在线官网  |   会议  |   在线投稿  |   购买纸书  |   科技图书馆

中南大学出版社 技术支持 版权声明   电话:0731-88830515 88830516   传真:0731-88710482   Email:administrator@cnnmol.com

互联网出版许可证:(署)网出证(京)字第342号   京ICP备17050991号-6      京公网安备11010802042557号