The Effect of Sm2O3 on the Chemical Stability of Borosilicate Glass and Glass Ceramics
来源期刊：Journal Of Wuhan University Of Technology Materials Science Edition2014年第4期
论文作者：张永强 WANG Mitang LI Mei WANG Ming 刘全生
文章页码：692 - 697
摘 要：Sm2O3 containing zinc-borosilicate glass and glass ceramics were prepared by melt quenching method, and the effect of Sm2O3 and micro-crystallization on the chemical stability of borosilicate glass was explored. DTA analysis showed that the endothermic peak and exothermic peak of basic glass changed from 635 ℃ and 834 ℃ to 630 ℃ and 828 ℃ respectively as a result of the doping of Sm2O3. XRD analysis showed the promoting effect of Sm2O3 on crystallization ability of this glass. The cumulative mass loss of base glass, Sm2O3 containing glass, glass ceramic and Sm2O3 containing glass ceramic was 0.289, 0.253, 0.329, 0.269 mg/mm2 respectively after 26 days corrosion in alkali solution, and 1.293, 1.290, 0.999, 1.040 mg/mm2 respectively in acidic erosion medium. Micro-crystallization decreased and improved the alkali and acid resistance of borosilicate glass respectively, the addition of Sm2O3 increased the alkali resistance of base glass and glass ceramics, and the slight effect of Sm2O3 on the acid resistance of borosilicate glass was also observed.
张永强1,2，WANG Mitang3，LI Mei3，WANG Ming3，刘全生1
1. School of Chemical Engineering, Inner Mongolia University of Technology2. School of Chemistry and Chemical Engineering, Inner Mongolia University of Science and Technology3. School of Materials and Metallurgy, Inner Mongolia University of Science and Technology
摘 要：Sm2O3 containing zinc-borosilicate glass and glass ceramics were prepared by melt quenching method, and the effect of Sm2O3 and micro-crystallization on the chemical stability of borosilicate glass was explored. DTA analysis showed that the endothermic peak and exothermic peak of basic glass changed from 635 ℃ and 834 ℃ to 630 ℃ and 828 ℃ respectively as a result of the doping of Sm2O3. XRD analysis showed the promoting effect of Sm2O3 on crystallization ability of this glass. The cumulative mass loss of base glass, Sm2O3 containing glass, glass ceramic and Sm2O3 containing glass ceramic was 0.289, 0.253, 0.329, 0.269 mg/mm2 respectively after 26 days corrosion in alkali solution, and 1.293, 1.290, 0.999, 1.040 mg/mm2 respectively in acidic erosion medium. Micro-crystallization decreased and improved the alkali and acid resistance of borosilicate glass respectively, the addition of Sm2O3 increased the alkali resistance of base glass and glass ceramics, and the slight effect of Sm2O3 on the acid resistance of borosilicate glass was also observed.
关键词：