Stress-strain Model of Corroded Concrete under Uniaxial Compressive Loading

来源期刊:Journal Of Wuhan University Of Technology Materials Science Edition2010年第2期

论文作者:陈朝晖 黄河

文章页码:303 - 307

摘    要:The prism specimens of corroded concrete were subjected to uniaxial compressive load to develop the stress-strain model. Compared to the un-corroded concrete, the mechanical prop- erties of corroded concrete, such as peak strength, Young’s modulus, and residual deformation, et al are degraded. The concrete, which were subjected to the aggressive media in the environment, were resulted in randomly distributed pre-loading flaws and defects. The propagation of these corrosion flaws during the procedure of loading was the main reason of degradation of corroded concrete properties. By the application of the statistic theory of continuum damage, the compressive stress-strain curve of corroded concrete was simulated. The initial damage factor was introduced to represent the corrosive effects of different media. The present damage constitutive model agreed well with the test results.

详情信息展示

Stress-strain Model of Corroded Concrete under Uniaxial Compressive Loading

陈朝晖1,2,黄河1

1. College of Civil Engineering, Chongqing University2. Ministry of Education Key Laboratory of Construction and New Technology of Mountain City

摘 要:The prism specimens of corroded concrete were subjected to uniaxial compressive load to develop the stress-strain model. Compared to the un-corroded concrete, the mechanical prop- erties of corroded concrete, such as peak strength, Young’s modulus, and residual deformation, et al are degraded. The concrete, which were subjected to the aggressive media in the environment, were resulted in randomly distributed pre-loading flaws and defects. The propagation of these corrosion flaws during the procedure of loading was the main reason of degradation of corroded concrete properties. By the application of the statistic theory of continuum damage, the compressive stress-strain curve of corroded concrete was simulated. The initial damage factor was introduced to represent the corrosive effects of different media. The present damage constitutive model agreed well with the test results.

关键词:

<上一页 1 下一页 >

有色金属在线官网  |   会议  |   在线投稿  |   购买纸书  |   科技图书馆

中南大学出版社 技术支持 版权声明   电话:0731-88830515 88830516   传真:0731-88710482   Email:administrator@cnnmol.com

互联网出版许可证:(署)网出证(京)字第342号   京ICP备17050991号-6      京公网安备11010802042557号